1) chrome oxide bricks
铬砖
1.
Float glass made by Luoyang Float Glass Limited Company and chrome oxide bricks((w(Cr_2O_3))>94%) made by Guang Dong Shijing Special Refractory Materials Works were adopted as test materials.
用广东石井特种耐火材料厂生产的铬砖(w(Cr2O3)>94%)和洛阳浮法玻璃有限公司生产的浮法玻璃作为试验材料,使用X射线荧光分析、扫描电子显微镜分析了侵蚀铬砖后玻璃液中Cr2O3的含量和铬砖表层显微结构,研究了侵蚀速率与侵蚀温度、侵蚀时间的相互关系。
2.
Float blue glass made by Luoyang Float Glass Limited Company and chrome oxide bricks made by Guang Dong Shijing Special Refractory Materials Works were adopted as test materials.
用广东石井特种耐火材料厂生产的铬砖(Cr_2O_3>94%)和洛阳浮法玻璃有限公司生产的蓝色浮法玻璃为实验材料,参照GB 1020488《玻璃熔窑用耐火材料在静态下抗玻璃液侵蚀实验方法》,使用扫描电子显微镜测试分析手段,研究了侵蚀前后铬砖显微结构和侵蚀界面附近元素组成的变化,探索了铬砖的耐侵蚀机制。
2) magnesia and low-level chrome brick
低铬镁铬砖
3) Magnesia-chrome brick
镁铬砖
1.
Destruction mechanism of magnesia-chrome bricks for different kinds of high-temperature furnace
不同类型高温窑炉用镁铬砖损毁机理分析
2.
This paper describes the influence of production condition of the dry-process cement rotary kiln on the service life of the magnesia-chrome brick.
为了实现我国大型干法水泥回转窑烧成带用直接结合镁铬砖的国产化,本文分析了干法水泥生产工艺条件对镁铬砖使用寿命的影响,总结了国外对镁铬砖损毁机理的研究结果,优化了水泥窑用直接结合镁铬砖的原料及生产工艺,研制出性能优异的大型干法水泥窑用直接结合镁铬砖LZMGe-8A。
4) alumina-magnesia-chrome refractory
铝镁铬砖
5) Magnesia chrome brick
镁铬砖
1.
Chemical property and detoxifcation of hexavalent chromium contained in magnesia chrome brick used in cement kiln;
水泥窑用镁铬砖中Cr~(6+)化合物的化学性质和解毒
6) chrome-corundum brick
铬刚玉砖
1.
In this paper a new technology of making chrome-corundum brick is introduced.
铬刚玉砖一般采用浇注成型或采用熔铸成型的工艺生产,但是这两种生产工艺分别存在着成本较高,生产效率较低、颗粒分布不够均匀等不足。
补充资料：铬砖
分子式：
CAS号：
性质：用铬矿制成的Cr2O3的含量大于30％的耐火材料。为了提高砖的高温性能，一般在料中加入10％以上的镁砂。铬砖属于中性砖，高温下与酸性和碱性耐火材料的作用都很弱，它的荷重软化温度和抗热震性都低于镁铬砖。主要用于高温下酸性和碱性耐火材料的隔离层，也用于有色冶炼炉的炉衬，但不宜用于直接与铁水接触而气氛又变化频繁的地方。铬砖现在已很少生产。
CAS号：
性质：用铬矿制成的Cr2O3的含量大于30％的耐火材料。为了提高砖的高温性能，一般在料中加入10％以上的镁砂。铬砖属于中性砖，高温下与酸性和碱性耐火材料的作用都很弱，它的荷重软化温度和抗热震性都低于镁铬砖。主要用于高温下酸性和碱性耐火材料的隔离层，也用于有色冶炼炉的炉衬，但不宜用于直接与铁水接触而气氛又变化频繁的地方。铬砖现在已很少生产。