1) chrome-free bricks
无铬砖
2) chromite-free basic brick
无铬碱性砖
1.
Elimination of chrome-pollution and utilization of substitute fuels in cement kilns have been causing successful substitution of magnesia chromite brick by chromite-free basic bricks consisted of dolomite brick, magnesia spinel brick and magnesia zirconia brick.
消除铬公害和在水泥窑内应用代用燃料促使白云石砖、尖晶石砖和镁锆砖组成的系列无铬碱性砖成功地替代着镁铬砖。
3) chrome oxide bricks
铬砖
1.
Float glass made by Luoyang Float Glass Limited Company and chrome oxide bricks((w(Cr_2O_3))>94%) made by Guang Dong Shijing Special Refractory Materials Works were adopted as test materials.
用广东石井特种耐火材料厂生产的铬砖(w(Cr2O3)>94%)和洛阳浮法玻璃有限公司生产的浮法玻璃作为试验材料,使用X射线荧光分析、扫描电子显微镜分析了侵蚀铬砖后玻璃液中Cr2O3的含量和铬砖表层显微结构,研究了侵蚀速率与侵蚀温度、侵蚀时间的相互关系。
2.
Float blue glass made by Luoyang Float Glass Limited Company and chrome oxide bricks made by Guang Dong Shijing Special Refractory Materials Works were adopted as test materials.
用广东石井特种耐火材料厂生产的铬砖(Cr_2O_3>94%)和洛阳浮法玻璃有限公司生产的蓝色浮法玻璃为实验材料,参照GB 1020488《玻璃熔窑用耐火材料在静态下抗玻璃液侵蚀实验方法》,使用扫描电子显微镜测试分析手段,研究了侵蚀前后铬砖显微结构和侵蚀界面附近元素组成的变化,探索了铬砖的耐侵蚀机制。
4) magnesia and low-level chrome brick
低铬镁铬砖
5) Magnesia-chrome brick
镁铬砖
1.
Destruction mechanism of magnesia-chrome bricks for different kinds of high-temperature furnace
不同类型高温窑炉用镁铬砖损毁机理分析
2.
This paper describes the influence of production condition of the dry-process cement rotary kiln on the service life of the magnesia-chrome brick.
为了实现我国大型干法水泥回转窑烧成带用直接结合镁铬砖的国产化,本文分析了干法水泥生产工艺条件对镁铬砖使用寿命的影响,总结了国外对镁铬砖损毁机理的研究结果,优化了水泥窑用直接结合镁铬砖的原料及生产工艺,研制出性能优异的大型干法水泥窑用直接结合镁铬砖LZMGe-8A。
6) alumina-magnesia-chrome refractory
铝镁铬砖
补充资料：电熔再结合镁铬砖
分子式：
CAS号：
性质：又称熔粒镁铬砖。高温性能介于熔铸镁铬砖和烧结镁铬砖之间，其荷重软化温度可达1700℃。一般先以轻烧氧化镁和铬矿为原料，用电弧炉将其熔融制成电熔镁铬砂，再经破碎、粉磨、配料、成型、烧成而制得。这种砖的应用领域和普通镁铬砖相近。