2) transcrystalline fracture
穿晶断裂
3) transgranular fracture
穿晶断裂
1.
Scanning electron microscopy (SEM) observation indicated that the fracture mode of this nanocomposite is mainly transgranular fracture, and many grain pull outs existed on its fracture surface.
SEM观察表明,Al2O3/TiC纳米复合陶瓷刀具材料的断裂方式主要是穿晶断裂,材料的断口处存在大量的晶粒拔出。
2.
The fracture type of the pure molybdenum bar with good transverse ductility is mainly a transgranular fracture type and net-type, which is characterized by a large amount of cleavage planes and river patterns.
在此过程中,镦态纯钼棒中形成的位错胞亚结构逐渐合并形成许多细小亚晶;纯钼棒经锻造镦粗变形后断口以穿晶断裂为主,具有明显的河流状花样和解理台阶,解理面上出现大量塑性变形的撕裂岭,且形成鱼网状的韧窝。
3.
The fracture type of pure Mo is intergranular fracture,the enhancement of the crack propagation stress of the Mo-C alloy is due to the addition of carbon,which makes the fracture type change to a transgranular fracture type.
结果表明:1号Mo-C棒中C含量(摩尔分数)为290×10-6,O含量为25×10-6,2号Mo-C棒中C含量为150×10-6,O含量为25×10-6;在同样条件下,2号Mo-C棒的横向弯曲性能更好;2号Mo-C棒的再结晶温度为950～1100℃左右;随着退火温度的升高,合金的横向弯曲性能逐渐提高,在1100℃时,合金的横向弯曲伸长率最高,达到10%;纯钼的断裂方式以沿晶断裂为主,添加C后,合金的裂纹扩展应力得到提高,合金的断裂方式变成以穿晶断裂为主,断口上有大量的解理面,具有明显的河流状花样和解理台阶;当添加的C含量偏高时,合金中生成大颗粒的碳化物,这种大颗粒的碳化物降低了合金的塑性。
4) transgranular facet
穿晶刻面
1.
The transgranular facets were identified as {111} γ , on which the intersecting angle between bands is 60°.
穿晶脆断刻面是｛１１１｝γ，刻面上滑移带相交成６０°，两相交大角度１０９°２８′的｛１１１｝γ穿晶刻面上滑移带成对称状；沿形变孪晶界面脆断面为｛１１０｝面，相交形变孪晶夹角为７０°；滑移带在孪晶晶界处产生扭折，扭折角３５～４０°；在任意的金相断面上，相交滑移带夹角是６０～８０
5) Transgranular brittle fracture
穿晶脆断
6) grain boundarytunneling
晶界隧穿
补充资料：穿晶开裂
分子式：
CAS号：
性质：金属材料开裂的金属学特征之一。裂纹由晶粒内部穿过。延性断裂的断口微观特征一般为韧窝状，脆性断裂的特征为解理或准解理花样。
CAS号：
性质：金属材料开裂的金属学特征之一。裂纹由晶粒内部穿过。延性断裂的断口微观特征一般为韧窝状，脆性断裂的特征为解理或准解理花样。