1) Binary monomers-grafted films
二元接枝膜
1.
Binary monomers-grafted films with temperature-and pH-sensitivities were prepared by photo-grafting of N,N-diethyl-acrylamide and acrylic acid onto polypropylene films with benzophenone(BP) as an initiator.
以二苯甲酮为引发剂,聚丙烯薄膜(CPP)为基材,通过紫外光接枝的方法制备了具有温度和pH值双重敏感特性的聚N,N-二乙基丙烯酰胺(PNDEA)与聚丙烯酸(PAA)二元接枝膜。
2) humidity sensor of grafted film
接枝膜湿敏元件
3) grafted membrane
接枝膜
1.
The machanical strength,resistance rate,expansion rate in alkaline electrolyte and alkaline absorbance of polyethylene-MAA grafted membrane were reported.
介绍了采用高压聚乙烯薄膜经γ射线辐照,然后在70℃的30%甲基丙烯酸的甲苯溶液中反应接枝的制备方法;报导了聚乙烯-MAA接枝膜的机械强度、电阻率、在碱液中的膨胀度以及吸碱液率等性能。
4) silane grafting EPM
硅烷接枝二元乙丙橡胶
1.
The EPDM/MVQ was modified by using the silane grafting EPM (EPM g S) as the compatibilizer and the modification mechanism was discussed.
探讨了硅烷接枝二元乙丙橡胶 (EPM g S)作相容剂对EPDM/甲基乙烯基硅橡胶 (MVQ)共混物的改性及改性机理。
5) three units graft
三元接枝
1.
In allusion to the problem that CR adhesive and the adhesive of two unites graft copolymerization of CR/MMA are low felting and peeling intension,we prepared the adhesive of three units graft copolymerization of CR/MMA/SBS, and determined the properties of the adhesive.
针对CR和CR/MMA二元接枝共聚胶粘剂初粘力低、剥离强度低这一问题 ,研制了CR/MMA/SBS三元接枝共聚胶粘剂 ,并测定了该胶粘剂的有关物性 。
6) graft polyol
接枝多元醇
补充资料：甲基丙烯酸甲酯-丙烯腈-丁二烯-苯乙烯接枝共聚物
分子式：
CAS号：
性质： 甲基丙烯酸甲酯、丙烯腈、丁二烯和苯乙烯的四元接枝共聚物。其连续相是甲基丙烯酸甲酯、丙烯腈和苯乙烯的三元共聚物，它接枝在分散相聚丁二烯上。透明、韧性好、耐冲击、有相当的热稳定性。除了透明性外，其性能和ABS很相似。将聚丁二烯橡胶溶解或分散在甲基丙烯酸甲酯、丙烯腈和苯乙烯的单体混合物中，在本体或悬浮体系中进行接枝聚合制备。主要应用于需要韧性、透明、高冲击、热稳定的材料领域，如电子仪表零件、矿灯等。