1) polybasic graft copolymerization
多元接枝共聚
2) CR/SBS/MMA/BA polybasic graft copolymerization
CR/SBS/MMA/BA多元接枝共聚
4) ternary starch graft copolymer
三元接枝共聚物
1.
The ternary starch graft copolymers are synthesized by inverse emulsion polymerization with cassava starch,acrylic acid(AA) and acrylamide(AM) as raw material and potassium permanganate as the initiator.
以淀粉为主要原料,丙烯酰胺、丙烯酸为接枝单体,采用反相乳液聚合方法合成了改性淀粉三元接枝共聚物;考察了交联剂、引发剂浓度、单体配比、中和度、反应温度等因素对淀粉-丙烯酸-丙烯酰胺三元接枝共聚物吸水性能的影响。
5) tetrabasic graft copolymerization
四元接枝共聚
1.
the SBS tetrabasic graft copolymerization was studied and effects of the monomer ratio,amount of AA and BPO,solidifying technology on adhesive properties were discussed,and the convenient adhesive with good properties for polyolefine was prepared.
研究了SBS四元接枝共聚反应 ,讨论了MMA/BA配比 ,AA和BPO用量、反应时间和反应温度及固化工艺对粘接性能的影响 ,并制得了性能优良、使用方便的聚烯烃用粘合剂。
6) graft polyether polyol
接枝聚醚多元醇
补充资料：氯乙烯和乙烯僧酸乙烯共聚物接枝共聚物
分子式：
CAS号：
性质：为在乙烯/醋酸乙烯共聚物(EVA)之大分子链上进行氯乙烯接枝共聚后得到之产品，按EVA中醋酸乙烯含量不同和接枝共聚物中EVA含量不同以及分子量大小，分为冲击改性剂用、硬质和软质品用三类。作冲击改性剂用和软质品用者多为EVA中VAC含量45％，EVA含量为50％。主要用于防水卷材、医用制品、电缆、记录材料和与PVC共混后作门窗型材。硬质品用者为EVA中VAC含量为15％，EVA含量5％～10％。除接枝物外含聚氯乙烯均聚物。可直接用作门窗型材和管材，冲击强度比一般PVC可提高4倍以上，将EVA溶于或分散于氯乙烯单体中进行悬浮聚合制得。
CAS号：
性质：为在乙烯/醋酸乙烯共聚物(EVA)之大分子链上进行氯乙烯接枝共聚后得到之产品，按EVA中醋酸乙烯含量不同和接枝共聚物中EVA含量不同以及分子量大小，分为冲击改性剂用、硬质和软质品用三类。作冲击改性剂用和软质品用者多为EVA中VAC含量45％，EVA含量为50％。主要用于防水卷材、医用制品、电缆、记录材料和与PVC共混后作门窗型材。硬质品用者为EVA中VAC含量为15％，EVA含量5％～10％。除接枝物外含聚氯乙烯均聚物。可直接用作门窗型材和管材，冲击强度比一般PVC可提高4倍以上，将EVA溶于或分散于氯乙烯单体中进行悬浮聚合制得。