1) Die Casting-forging Method
压铸锻造双控成形
2) Combination Process of Die Casting and Forging
铸锻双控成形
1.
Research on the comparison of the macroscopic defect and the mechanical property of AZ91D magnesium alloy parts produced by liquid combination process of die casting and forging and liquid die casting;
AZ91D镁合金铸锻双控成形与压铸制件宏观缺陷及力学性能的对比研究
2.
The liquid combination process of die casting and forging is a new forming method which combines processing property of die casting with that of forging.
液态铸锻双控成形是综合了压力铸造和锻造的工艺特性而提出的一种新的成形方法。
4) Casting-forging double control forming
铸锻双控成型
5) forging forming
锻造成形
1.
Wrought magnesium alloys and several key factors affecting the forging forming;
锻造镁合金及影响锻造成形的几个关键因素
6) metal forging
锻造成形
1.
This paper reviews the theory of rigid-plastic/rigid-viscoplastic FEM, the key techniques of FEM simulation and the method of FEM simulation in metal forging.
介绍了锻造成形数值模拟中的刚(粘)塑性有限元法的基本理论,对模具型腔信息描述、网格划分、边界条件处理等数值模拟中的关键技术做了全面系统的总结,分析比较了处理上述问题的各种方法。
补充资料：主要射出成形材料成形时应注意事项
■主要射出成形材料成形时应注意事项
品 名 注 意 事 项
PVC
聚氯乙烯
1. 产品种类范围非常广（硬质、软质、聚合物等），成型条件各有不同，从熔融至分
解之温度范围很小，尤须注意加热温度。
2. 附着水分少，但成型周期尽可能减少（50℃~60℃热风干燥）。
3. 成型机方面，与材料直接接触的部位须电镀或采用不锈钢以防热分解所产生的盐酸
侵蚀。射出压力2100kg/cm2程度。
4. 所有塑料当中必须是细心注意温度调节。
5. 浇口附近易产生流纹，故射出操作后，柱塞不要后退使浇口充分固化后再瞬间退后为宜。
6. 加热之初温不宜高，特别注意熔融情形。第二级加热温度较高，且尽可能使成形周
期缩短，比较安全。
PA
聚醯胺树脂
1. 成型温度比其它材料高，故采用油加热的成形机较适当。
2. 吸湿性大，必须充分干燥。水分对成型品的品质影响甚大（80℃热风干燥约5~6小时）。
3. 须退火以消除内部歪斜。
PP
聚丙烯
1. 同PE，但成形温度必须较高。熔融温度170℃，超过190℃则流动性大增，则毛边增加，
易产生接缝及凹入情形。
PC
聚碳酸脂
1. 吸湿性比尼龙小，但若有些微之水分存在则成型品产生其它色泽或气泡，故必须密封
干燥同时成形时也须预备干燥（120℃之温度4小时）。
2. 加热温度超过320℃时则产生热分解，成品变色，故特别注意温度调节，又成型时的温度调节也非常重要，须特别注意其最低温度、最低时间。
3. 须退火以消除内部歪斜（130℃~135℃，1小时程度为准）。