1) NbTi superconducting wire
NbTi超导线材
1.
Development of shaft furnace for vacuum and N_2 shielded heat-treatment of NbTi superconducting wires;
NbTi超导线材井式真空氮气保护热处理炉的研制
2) NbTi superconducting strand
NbTi超导股线
1.
Method on the critical current test of NbTi superconducting strand for ITER;
用于ITER的NbTi超导股线临界电流测试方法
3) NbTi superconductor
NbTi超导体
5) superconducting wires
超导线材
1.
The MgB2/Fe superconducting wires were fabricated by the ex-situ Powder-In-Tube (PIT) process.
采用先位法将MgB2粉装入纯铁管中,制备出MgB2/Fe超导线材。
6) MgB_2 wires
MgB2超导线材
1.
Phase compositions, microstructure features, chemical components and critical current density (J_c) of the doped and the undoped MgB_2 wires are investigated by using X-ray diffractometer, scanning electron microscopy, energy dispersive spectrometer and the standard four-probe resistance technique, respectively.
以低碳钢管为包套材料,采用原位粉末套管法制备出5mol%TiB2掺杂的MgB2超导线材。
补充资料：超导线材的剩余电阻比测定
超导线材的剩余电阻比测定
measurement of residual resistance ratio in composite superconducting wire
试样图1剩余电阻比测定示意则测得的样品室温电阻值与低温下的电阻值之比为超导材料稳定化基材的剩余电阻比。国际上商品化的超导材料的剩余电阻比常在120一150。一般对于氢泡室、核磁共振人体成象装置等低场使用的超导磁体，对剩余电阻比的要求较高;而对于高场使用的超导磁体，对所使用的超导材料的剩余电阻比的要求则可以降低，因为此时磁场对铜、铝的电阻的影响将起主要作用。n 工n，一..1 ︵口甲。一X︶寰┌─┬───┬─┬─┬───┬──┬─┐│ │ │ │ │ │ │ │├─┼───┼─┼─┼───┼──┼─┤│ │洲 │ │ │J.训甲│声声│尸││ │ ├─┼─┼───┤ │ ││ │ │( │ │ │ │ │├─┼─┬─┼─┼─┼───┼──┼─┤│ │ │ │ │ │ │ │ │├─┼─┼─┼─┼─┼───┼──┼─┤│ │ │ │ │ │ │ │ │├─┼─┼─┼─┼─┼───┼──┼─┤│ │ │ │ │ │ │ │ │└─┴─┼─┼─┼─┼───┼──┼─┤ │. │ │ │ │ │ │ └─┴─┴─┴───┴──┴─┘12 16 20 24 28 32 温度(K、图2 NbTi样品电阻随温变化曲线(华崇远)超导线材的剩余电阻比测定measurement ofresidual resistance ratioin eomPosite supereonduet-ing wire超导线材在室温时的电阻率与在4 .ZK时电阻率之比，即肠。。K/脚.2K称为材料的剩余电阻比。 在金属和合金中，电阻是由晶格对于自由电子的散射所造成的，即电阻率可由如下公式表达 p=肠+p(T)式中第二项p(T)主要反映了晶格的振动对于电子散射的影响，是随温度而变化的。在室温时这一项占主要地位。第一项两反映了晶格的畸变对于电子散射的影响，它和晶格的位错及杂质元素等有关。随着温度降到液氦温度附近，第二项的作用趋于零，而第一项的作用占主要地位。结果金属的电阻呈现出不随温度而变化的特点，这就是剩余电阻。 由于在超导材料中磁通蠕动和局部的磁通跳跃是本征性的，不可避免的，为防止由此而引起的超导状态的碎灭，实用超导材料如NbTi、Nb3Sn等都需要在超导体外面覆以铜、铝等稳定化材料以增加超导体的稳定性。