1) primary spacing
一次间距
1.
It is shown that with the increase of growth velocity,the primary spacing decreases to a local minimum value first,and then increases to a local maximum value,finally decreases again.
48％水杨酸苯酯(Salol)(质量分数)进行恒速定向凝固实验,考察了一次间距、尖端半径和尖端温度随凝固生长速度变化的规律。
2.
the experimental studies of primary spacing in directionally solidified succinomitrile-1.
从凝固界面形态演化的时间相关性和路径相关性的角度,对一次间距问题进行了实验研究,发现了一些新的现象,并由此对一次间距的理论模型和实验研究方法进行了分析讨论。
3.
A cellular automaton model was developed to simulate the primary spacing selection of dendritic array during directional solidification.
发展了一个元胞自动机模型来模拟定向凝固中枝晶阵列的一次间距选择。
2) primary dendrite arm spacing
一次枝晶间距
1.
Effect of Al-Cu alloys diameter on thermal gradient and primary dendrite arm spacing during directional solidification;
试样直径对Al-Cu合金定向凝固温度梯度和一次枝晶间距的影响
2.
At withdrawn rate of 50μm/s,the primary dendrite arm spacing is decreased from 177μm to 150μm and 125μm when the superheating temperature is increased from 1500℃to 1640℃and 1780℃respectively,theγ′are refined in both dendrite c.
结果表明:合金熔体在1380—1650℃发生一系列的结构变化;当抽拉速率为50μm/s时,随熔体超温处理温度由1500℃升至1640和1780℃,合金一次枝晶间距由177μm分别减至150和125μm,枝干与枝间γ′相的尺寸减小,且枝间γ′相形貌变得规整。
3.
The results show that the primary dendrite arm spacing of the superheated samples at 950 and 1 050 ℃ decreases 31.
结果表明:经过950℃和1 050℃过热处理的一次枝晶间距比在750℃常规过热直接定向凝固的分别减小了31。
3) primary dendrite spacing
一次枝晶间距
1.
The calculation formulation of primary dendrite spacing for Al-4.
5%Cu合金凝固的一次枝晶间距计算公式进行了讨论,并结合定向凝固条件,研究各种条件参数对计算结果的具体影响。
2.
Several models of primary dendrite spacing for binary alloy were reviewed.
本文评述了二元系统一次枝晶间距模型的发展及特点,并验证了在多元合金系统中的适用性,结果表明,在 DD8单晶高温合金中,λ_1-G 关系符合二元系统模型,但λ_1-V 关系和二元系统模型有较大的偏离,λ_1为一次枝晶间距,G 为温度梯度,V为凝固速率。
4) primary dendrite spacing
一次分枝间距
1.
4%Mg alloys on the mor-phology of dendrite α phase was investigated and the amount of dendrite αphase and the characteristic parameters, the primary dendrite spacing and secondary dendrite arm spacing, were also measured.
4％Mg两种近共晶成分铸造合金,考察了Sr的加入对组织中α枝晶形态的影响,测量了完全变质合金中α枝晶相数量及α枝晶的特征参数:一次分枝间距和二次枝臂间距。
2.
The characteristic parameters of dendritic α phase in near-eutectic Al-Si alloys modified with varying strontium, primary dendrite spacing and secondary dendrite arm spacing, were measured and the changes of the mechanical properties with these parameters were considered.
测量了用不同Sr加入量变质的近共晶Al Si合金中枝晶α Al的一次分枝间距和二次枝晶臂间距 ,考察了枝晶α Al特征参数的变化对合金力学性能的影响。
5) primary dendritic spacing
一次枝晶间距
1.
Based on the present experimental observations and the known dendritic models, a numerical statistical model of primary dendritic spacing is first presented to the dendritic array in directional solidification at constant velocity.
从统计学随机性和动力学必然性的角度，通过对定向凝固界面形态演化过程的分析，结合现有的实验观察与已有的枝晶模型，采用统计学随机模拟的方法提出了一个在恒速定向凝固条件下列状晶生长一次枝晶间距的数值统计模型，模型所得数值结果与实验结果吻合得很好。
2.
5Cu alloy,history-dependent selection of the primary dendritic spacing is systematically investigated by the experimental method of step-variation in growth rate.
5Cu单晶进行台阶变速定向凝固实验，考察了金属合金中一次枝晶间距随凝固生长速度变化的动态响应规律。
3.
0 wt─% acetone,is directionally solidified to investigate the dynamic response of primary dendritic spacing to the variation of the solidification parameters (i.
０ｗｔ─％丙酮进行定向凝固实验，考察了一次枝晶间距随凝固控制参数（生长速度ｖ和温度梯度Ｇ）变化的动态响应规律，发现一次枝晶间距选择一个较宽的分布范围，而平均一次间距具有明显的历史相关性，将实验结果与主要理论模型进行了比较。
6) Primary Dendritic Arm Spacing
一次枝晶臂间距
补充资料：板间距
分子式：
CAS号：
性质：又称板间距。板式塔相邻两块塔板之间的距离。塔板间距直接影响塔的高度，并对适宜气速的确定发生重要影响。塔板间距的大小与塔的处理能力、操作弹性、塔板效率和塔径大小密切相关。对塔板数较多或安装在室内的塔，可考虑采用较小的塔板间距，适当增大塔径而降低塔高，若塔板数不多，则塔板间距较大而塔径较小的塔比较经济。当塔内各段负荷不同时，可考虑各板采用不同的塔板间距。
CAS号：
性质：又称板间距。板式塔相邻两块塔板之间的距离。塔板间距直接影响塔的高度，并对适宜气速的确定发生重要影响。塔板间距的大小与塔的处理能力、操作弹性、塔板效率和塔径大小密切相关。对塔板数较多或安装在室内的塔，可考虑采用较小的塔板间距，适当增大塔径而降低塔高，若塔板数不多，则塔板间距较大而塔径较小的塔比较经济。当塔内各段负荷不同时，可考虑各板采用不同的塔板间距。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条