1) anodic polarization curve
阳极极化曲线
1.
The corrosion resistance of Ni-W-P-SiC,a pulsely electro-deposited composite coating was evaluated by means of immersion experiment,anodic polarization curves and neutral salt-spray corrosion test.
采用腐蚀溶液浸泡、阳极极化曲线和中性盐雾试验3种方法较系统地研究了Ni-W-P-SiC脉冲复合镀层的耐蚀性。
2.
The influence of chloride ions and sulfide ions on 304 and 316L stainless steel (SS) respectively in the simulated cooling water system is studied by using anodic polarization curves.
利用阳极极化曲线测定了模拟冷却水体系中氯离子和硫离子对304不锈钢和316L不锈钢耐蚀性能的影响,结果显示:在实验条件下,304不锈钢受氯离子作用而点蚀的浓度界限约为150 mg/L,316L不锈钢约为250 mg/L;在相同水体中,316L不锈钢的点蚀电位明显高于304不锈钢;以[C l-]/[SO42-](mg/L)比值作比较,对304不锈钢,当[C l-]/[SO42-](mg/L)≤0。
3.
Anodic polarization curve experiments show that for the electrodeposited Ni Mo P alloys, the nickel mol fraction of which has in between 0.
用失重法、阳极极化曲线、Ｘ光电子能谱（ＸＰＳ）以及俄歇电子能谱（ＡＥＳ）研究了电沉积ＮｉＭｏＰ合金镀层在５％ＮａＣｌ溶液中的腐蚀特性。
2) anode polarization curve
阳极极化曲线
1.
The corrosion rates and anode polarization curves of RE-Ni-W-P-SiC-PTFE composite electrodeposits as plated and after heat treatments at different temperature were studied respectively by using various concentrations of hydrochloric acid and ferric chloride solutions as corrosion media, and their anode polarization curves were compared with those of RE-Ni-W-P-SiC composite electrodeposits.
采用不同浓度的盐酸、FeCl3溶液为腐蚀介质,研究了RE-Ni-W-P-SiC-PTFE复合电镀层于镀态下及经不同温度热处理后的腐蚀速率与阳极极化曲线,并与RE-Ni-W-P-SiC复合电镀层的阳极极化曲线进行了比较。
2.
Through anode polarization curve and electrochemical impedance chart,comparison between influences of Cl and S ions on corrosion-resistance performance of passive film on 316L stainless steel in simulated cooling water was conducted.
根据阳极极化曲线和电化学阻抗谱 ,比较了模拟冷却水中氯离子和硫离子对 3 1 6L不锈钢钝化膜耐蚀性能的影响。
3) anodic polarization
阳极极化曲线
1.
Phosphating primer and anoding chemical conversion film were measured using 3 measurement of salt spray corrosion tests,potentiostatic anodic polarization curves and electrochemical impedance spectroscopy(EIS).
通过盐雾实验、稳态阳极极化曲线和电化学阻抗谱 3种测试方法 ,对磷化底漆和阿洛丁 (12 0 0 )化学转化膜进行了测试 ,结果发现磷化底漆的耐蚀性明显优于阿洛丁化学转化膜 。
2.
Anodic polarization curves of reinforcing bars in a simulation-pore solution containing sodium chloride and Sodium nitrite were made, and the results obtained were as follows:In case of no addition of sodium chloride steel embedded in concrete is in a passivation state of passivity and is not corroded.
通过掺氯化钠和亚硝酸钠的模拟混凝土孔溶液中钢筋阳极极化曲线的测定 ,发现未掺氯化钠混凝土中钢筋 ,钝化膜比较稳定 ,钢筋不易腐蚀。
5) anodic polarization current
阳极极化曲线<冶>
6) anodic steady polarization curve
阳极稳态极化曲线
补充资料：环状阳极极化曲线
分子式：
CAS号：
性质：钝性金属在含有氯离子的溶液中，用稳态慢速电位扫描方法，先向正电位方向，然后再向负电位方向扫描所测得的呈环状的阳极极化曲线。如图示(图暂缺)。Eb为孔蚀击穿电位，此时钝化膜开始破坏产生孔蚀；Ep为孔蚀保护电位，此时钝化膜重新愈合修补好，金属恢复钝态。这是表征金属对孔蚀敏感性的两个基本电化学参数，可评价金属的孔蚀倾向。
CAS号：
性质：钝性金属在含有氯离子的溶液中，用稳态慢速电位扫描方法，先向正电位方向，然后再向负电位方向扫描所测得的呈环状的阳极极化曲线。如图示(图暂缺)。Eb为孔蚀击穿电位，此时钝化膜开始破坏产生孔蚀；Ep为孔蚀保护电位，此时钝化膜重新愈合修补好，金属恢复钝态。这是表征金属对孔蚀敏感性的两个基本电化学参数，可评价金属的孔蚀倾向。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条