1) self-shielded metal cored wire for hardfacing
自保护金属芯堆焊焊丝
2) alloy powder surfacing with self-shielded flux-cored wire welding
自保护药芯焊丝外添加合金粉堆焊
1.
a new manufacturing process of large area wear-resistant composite board was developed, and the method was called: alloy powder surfacing with self-shielded flux-cored wire welding.
本文提出了一种大面积耐磨复合板的制造方法:自保护药芯焊丝外添加合金粉堆焊并进行研究。
3) self-shielded flux-cored wire
自保护药芯焊丝
1.
Development and property analysis of ultra-low carbon self-shielded flux-cored wire with nitride solid solution strengthening;
超低碳氮强化自保护药芯焊丝的研制及性能分析
2.
Influence of hydrogen on weld metal toughness by self-shielded flux-cored wire welding;
氢对自保护药芯焊丝焊缝金属韧度的影响
3.
Research on repairing of rail by self-shielded flux-cored wire without pre-heating;
自保护药芯焊丝在钢轨冷焊修复中的应用
4) self-shielded flux cored wire
自保护药芯焊丝
1.
Mechanism and influencing factors of spatter formation with self-shielded flux cored wire;
自保护药芯焊丝飞溅的形成机理及其影响因素
2.
Effects of O section profile on weldability of self-shielded flux cored wire;
0型截面外形对自保护药芯焊丝焊接性能的影响
3.
Effect of Fe_2O_3, on self-shielded flux cored wire;
Fe_2O_3对自保护药芯焊丝性能的影响
5) self shielded flux cored wire
自保护药芯焊丝
1.
This paper has expounded the importance and urgency of self shielded flux cored wire (SSFCW) study.
介绍了自保护药芯焊丝的特点 ,并指出加快自保护药芯焊丝研制的重要性和紧迫性 。
2.
The influence of three kinds of RE elements and RE metal mixture on the oxygen,nitrogen content and proe sensitivity in the weld of self shielded flux cored wire was investigated in the present study.
研究了三种稀土合金及混合稀土对自保护药芯焊丝熔敷金属中含氧量、含氮量、气孔敏感性的影响规律 ,通过试验及理论分析发现 ,增加稀土元素的添加量 ,可使熔敷金属中含氧量下降 ,降低了气孔敏感性 ,混合稀土的作用最明显 ,它完全抑制了气孔。
3.
The effect of aluminium on the pore sensitivity,microstructure,mechanical properties and inclusion of the deposited metal were studied by changing the amount of aluminium powder in the flux core and the aluminium content in the steel sheath of the self shielded flux cored wire.
通过自保护药芯焊丝药芯配方中铝粉加入量的变化、以及采用含铝和不含铝两种钢带作为焊丝外皮的变化 ,深入地研究了铝对焊缝气孔敏感性、熔敷金属力学性能、金相组织、夹杂物种类及形态的影响。
6) self-shielded flux cored arc welds
自保护药芯焊丝电弧焊
补充资料：自保护焊丝
自保护焊丝
self-shielded welding wire
2 1 b00hU honsi自保护焊丝(self一shielded welding wire) 不需外加气体或焊剂保护，仅依靠焊丝自身的合金元素及在高温时的反应来防止空气中的氧、氮等气体浸入和补充合金成分的专用焊丝。目前，自保护焊丝主要采用药芯焊丝，实芯焊丝应用很少。在药芯焊丝方面，按照其渣系的不同，可分为氟一铝型自保护焊丝、氟一钦型自保护焊丝、氟一钙型自保护焊丝和氟一钦一钙型自保护焊丝。前两种类型的焊接工艺性能良好，应用较广泛;后两种的焊缝韧性得到改善，但焊接工艺性能较差。为保证充分脱氧、脱氮，在焊丝药芯中还加入了大量的铝、镁等强脱氧剂。为提高焊缝韧性，还可加入适量镍等。与手工电弧焊相比较，自保护焊的焊缝强度稍有提高，伸长率稍有降低，冲击韧性也不高，故不适干焊接重要结构。自保护焊丝已用于低碳钢、50kg级高强钢、不锈钢的焊接和耐磨堆焊。自保护焊接时烟尘很大，要加强通风换气措施。另外，对操作技能要求较高，掌握不当会引起接头性能波动。 (尹士科)