1) aluminum infiltration
熔渗Al
2) aluminizing
[英][ə'lju:minaiz] [美][ə'lumə,naɪz]
渗Al
1.
The results showed that the dense and consecutive diffusion layer could be prepared on the surface of the Mg alloy by the present process,and both aluminizing and the AI-Ce co-diffusing could improve the properties of anti-corrosi.
结果表明,本方法可在镁合金表面获得连续、致密的表面渗层,渗Al及Al-Ce共渗层均能提高镁合金的硬度及耐腐蚀性,Al-Ce共渗层的硬度及耐蚀性明显优于渗纯铝。
2.
Post-aluminizing was performed on the sputtered coating to improve the high-temperature oxidation resistance.
用SEM、XRD和EPMA等手段,研究了溅射NiCrAlY涂层渗Al前后在1000℃和1100℃的高温氧化行为。
3.
Post-aluminizing was performed on the sputtered coating to further upgrade its corrosion resistance.
采用SEM、XRD和EPMA等手段,研究了溅射NiCrAlY涂层渗Al前后在700℃盐和水蒸气下的腐蚀行为。
3) infiltration
[英][,infil'treiʃən] [美][,ɪnfɪl'treʃən]
熔渗
1.
Present progress of studies on interfacial modification in SiCp/Al composites fabricated by infiltration process;
无压熔渗制备SiCp/A l复合材料的界面改性研究进展
2.
Effect of Infiltration Pressure on Al-based Composites Reinforced by Si Particle;
熔渗压力对制备硅颗粒增强铝基复合材料的影响
3.
Preparing low-copper W-Cu alloys by infiltration;
熔渗法制备低铜W-Cu合金
4) melt infiltration
熔渗
1.
TiC-TiN-based, WC-based cermets were subjected to a hybrid treatment of melt infiltration and nitridation in high temperature and high pressure.
采用熔渗/氮化复合处理技术对TiC-TiN基、WC基金属陶瓷进行了高温高压熔渗/氮化处理,通过扫描电镜、能谱仪、X射线衍射等分析技术对其显微组织、成分及结构进行了分析。
2.
Ti(C,N)-based cermet was subjected to a multiple surface treatment of melt infiltration and nitridation at high temperature and high pressure.
对Ti(C,N)基金属陶瓷进行了高温高压熔渗/氮化复合表面处理,通过扫描电镜、能谱仪、X射线衍射等分析技术对其显微组织、成分及结构进行了分析,并对其处理前后的硬度进行了测试分析。
3.
In this paper,chemical pure nickel powder,titanium powder,aluminum powder,graphite powder as raw material,TiC/Ni3Al porous performs were prepared by self-propagating high temperature synthesis method(SHS),and pressureless melt infiltration method was used to preparing TiC/Ni3Al composites.
以化学纯镍粉、钛粉、铝粉、石墨粉为原料,采用燃烧合成方法制备了TiC/Ni3Al含孔预制件,用无压熔渗法制备了TiC/Ni3Al复合材料。
5) infiltrate
[英]['ɪnfɪltreɪt] [美]['ɪnfɪl'tret]
熔渗
1.
Based the requirement of property of CuWAlTe,we adopted special high-temperature infiltrate technology to meet the need of vacuum contactor,successfully resolved the loss of Te content in electric-alloy and passed by normal test.
根据真空接触器对CuWAlTe电触头的性能要求,采用特有的熔渗技术,成功解决了制备CuWAlTe时Te挥发引起的Te含量低的问题。
2.
This paper deals with the properties of high voltage switch CuW contact infiltrated under H2 atmosphere, and the affect factors are analyzed.
重点研究了H2 气氛熔渗方法制造的高压开关CuW触头材料的物理机械性能 ,分析了影响材料性能的因素。