1) porous ceramic preforms
多孔陶瓷预制体
1.
In this paper, the technology using quartz powder as starting materials and starch as foaming agents for preparing porous ceramic preforms is studied.
探索以SiO2为骨料,选择合适的助剂、烧成制度、成型压力和颗粒粒度,烧制成三维连通网格状多孔陶瓷预制体的工艺制度,用于自发浸渗熔融无机盐相变材料以制备无机盐/陶瓷基复合相变储能材料。
2) ceramic performs
陶瓷预制体
1.
The present paper summarizes the fabrication methods of the porous ceramic performs,and introduces the merit and weakness of those methods.
介绍了网络陶瓷预制体的制备方法及研究进展,分析了各种制备方法的特点。
3) porous ceramic support
多孔陶瓷支撑体
1.
Study on coating for silicon carbide porous ceramic support;
碳化硅多孔陶瓷支撑体表面涂层研究
2.
A porous ceramic support comprising alumina and a certain number of sintering aids was prepared by extrusion.
制备出管式多孔陶瓷支撑体 。
4) porous ceramic substrate
多孔陶瓷载体
1.
The prepared AlOOH sol will be used as a coating modifier for the porous ceramic substrate.
在以SB粉为原料,HNO3为解胶剂制得的稳定AlOOH溶胶中加入添加剂(PEG、PVA),对多孔陶瓷载体进行了表面涂层。
5) porous semiconductor ceramic
多孔半导体陶瓷
1.
Analyzed was the humid-sensing mechanism of porous semiconductor ceramic in low humidity range.
定量分析了多孔半导体陶瓷低湿度范围内的湿敏机理,通过理论推导,得出电阻与相对湿度关系的解析表达式。
6) porous ceramic
多孔陶瓷
1.
Fabrication of Porous Ceramic With Starch as the Pore-forming Agent;
以淀粉作造孔剂制备多孔陶瓷
2.
Preparation of TiO_2 porous ceramic;
TiO_2多孔陶瓷的制备
3.
Al_2O_3 matrix porous ceramics prepared by SHS;
燃烧合成法制备的Al_2O_3基多孔陶瓷
补充资料:多孔陶瓷支撑体膜
分子式:
CAS号:
性质:在多孔陶瓷体上附着的微孔陶瓷膜层。膜层厚度一般在几微米到几十微米,外径孔径一般为0.1~0.5μm,个别也有厚度达3~5μm、孔径10μm的。多采用氧化铝、二氧化钛和二氧化锆等作膜材料。制法是:用电机带动陶瓷支撑体旋转,当溶胶液(膜材料)滴落在支撑体上,就会迅速地敷覆到支撑体表面,待溶剂蒸发、凝胶化和干燥成膜后,经热处理而制成氧化物薄膜。现已为食品(含饮料)、医药、生物技术和环境保护等领域开发利用。
CAS号:
性质:在多孔陶瓷体上附着的微孔陶瓷膜层。膜层厚度一般在几微米到几十微米,外径孔径一般为0.1~0.5μm,个别也有厚度达3~5μm、孔径10μm的。多采用氧化铝、二氧化钛和二氧化锆等作膜材料。制法是:用电机带动陶瓷支撑体旋转,当溶胶液(膜材料)滴落在支撑体上,就会迅速地敷覆到支撑体表面,待溶剂蒸发、凝胶化和干燥成膜后,经热处理而制成氧化物薄膜。现已为食品(含饮料)、医药、生物技术和环境保护等领域开发利用。