1) Mo-Ni-Cu ternary system
Mo-Ni-Cu三元体系
2) Ni-Mo-Re ternary system
Ni-Mo-Re三元系
1.
The isothermal section and the components of the phase regions for Ni-Mo-Re ternary system at 1473 K was determined by means of diffusion triple and electron microprobe analysis.
采用三元扩散偶技术测定了Ni-Mo-Re三元系1473K的等温截面,借助电子探针微区成分分析方法分析了Ni-Mo-Re三元扩散偶的相区成分,并对其相关系进行了研究。
3) Ni-Fe-Mo ternary system
Ni-Fe-Mo三元系
1.
The isothermal section of Ni-Fe-Mo ternary system at 1373 K was determined by means of diffusion triple and electron probe microanalysis(EPMA).
采用三元扩散偶技术测定了Ni-Fe-Mo三元系1373K的等温截面,借助电子探针微区成分分析方法分析了Ni-Fe-Mo三元扩散偶的相区成分,并对其相关系进行了研究。
4) Ni-Cr-Mo ternary system
Ni-Cr-Mo三元系
1.
The isothermal section of Ni-Cr-Mo ternary system at 1358 K was determined by means of diffusion triple and electron microprobe analysis.
应用三元扩散偶技术测定了Ni-Cr-Mo三元系1358K的等温截面,借助电子探针微区成分分析方法分析了Ni-Cr-Mo三元扩散偶的相区成分,并对其相关系进行了研究。
5) Cu-Ni-Sn ternary system
Cu-Ni-Sn三元系
1.
Thermodynamic calculation of phase equilibria in Cu-Ni-Sn ternary system;
Cu-Ni-Sn三元系相平衡的热力学计算
补充资料：Cu-A1-Ni shape memory alloy
分子式：
CAS号：
性质：一种含A1 14％～14.5％(质量)、Ni 3％～4.5％(质量)、余者为铜的具有形状记忆效应和伪弹性的合金。其Ms点在133～373K之间。该合金的形状记忆应变约4％，它的热循环特性、形变循环特性和疲劳特性等均比TiNi形状记忆合金差。熔炼与Cu-Zn-A1形状记忆合金相同。该合金加工性很差，冷加工完全不可能。它的另一突出问题是随时间增长而记忆严重衰退的现象，为了提高合金的稳定性，可以进行等温淬火或一般淬火后进行时效处理。在Cu-A1-Ni形状记忆合金基础上开发出的Cu12Al5Ni2MnTi％(质量)五元高温形状记忆合金，铝含量降低，并加入Mn、Ti后，使Ms点提高到473K，同时合金的加工性亦得到改善，使Cu-A1-Ni系形状记忆合金成为具有实用价值的材料。
CAS号：
性质：一种含A1 14％～14.5％(质量)、Ni 3％～4.5％(质量)、余者为铜的具有形状记忆效应和伪弹性的合金。其Ms点在133～373K之间。该合金的形状记忆应变约4％，它的热循环特性、形变循环特性和疲劳特性等均比TiNi形状记忆合金差。熔炼与Cu-Zn-A1形状记忆合金相同。该合金加工性很差，冷加工完全不可能。它的另一突出问题是随时间增长而记忆严重衰退的现象，为了提高合金的稳定性，可以进行等温淬火或一般淬火后进行时效处理。在Cu-A1-Ni形状记忆合金基础上开发出的Cu12Al5Ni2MnTi％(质量)五元高温形状记忆合金，铝含量降低，并加入Mn、Ti后，使Ms点提高到473K，同时合金的加工性亦得到改善，使Cu-A1-Ni系形状记忆合金成为具有实用价值的材料。