1) Mo-Si-B ternary system
Mo-Si-B三元系
1.
The standard formation free energies at different temperatures of compounds in a Mo-Si-B ternary system were calculated.
计算了Mo-Si-B三元系中各化合物不同温度下标准生成自由焓和合成Mo5SiB2(T2相)反应在不同开始温度下的绝热温度及反应产物的熔化比。
2) Mo Si C ternary system
Mo-Si-C三元系
3) Mo-Si-C ternary system
Mo-Si-C三元体系
1.
Research on Mo-Si-C ternary system composites by use of DSC method;
Mo-Si-C三元体系复合材料的示差扫描量热法研究
4) Mo-Si-B in-situ composites
Mo-Si-B系原位复合材料
1.
Mo-Si-B in-situ composites are an important class of novel structural materials.
Mo-Si-B系原位复合材料是一族新型的高温结构材料,目前的研究主要集中在其中的α-Mo+Mo_3Si+Mo_5SiB_2(T_2)、Mo_5Si_3B_x(T1)+Mo_3Si+Mo_5SiB_2(T2)和Mo_5Si_3B_x(T1)+MoSi_2+MoB3个体系。
5) Mo-Si-B alloys
Mo-Si-B合金
1.
Impetus to intimate and advance the study of Mo-Si-B alloys is expected for this paper concerned.
详细综述了最近国外Mo-Si-B合金的研究进展。
2.
The elevated temperature oxidation behavior of Mo-Si-B alloys is reviewed in this article.
综述了Mo-Si-B合金高温氧化行为的研究进展。
补充资料：三元系压电陶瓷
分子式：
CAS号：
性质：三种ABO3型化合物形成的三元系压电陶瓷固溶体为主晶相的陶瓷材料。它比二元系压电陶瓷如锆酸铅-钛酸铅（PBZrO3-PbTiO3）具有烧成温度范围宽、气孔率低等特性。在PBZrO3-PbTiO3二元系基础上加入的第三种成分的各种组合，称“复合金属离子组合”。常用的三元系压电陶瓷有：铌镁酸铅系[xPb(Mg1/3Nb2/3)O3-yPbTiO3-zPbZrO3]，铌锌酸铅系[xPb(Zn1/3Nb2/3)O3-yPbTiO3-zPbZrO3]，铌锰酸铅系[xPb(Mn1/3Nb2/3)O3-yPbTiO3-zPbZrO3]，铌锑酸铅系[xPb(Sb1/2Nb1/2)O3-yPbZrO3]，锑锰酸铅系[xPb(Mn1/3Sb2/3)O3-yPbTiO3-zPbZrO3]等。除用含铅化合物作为第三组元外，还有非铅化合物。如A+1B+5O32—或A+3B+3O32—等。三元系压电陶瓷类型很多。在三组元基础上，再加入第四种或更多种ABO3型化合物，则组成四元系或多元系压电陶瓷。其用途十分广泛。可用于制作扩音器、滤波器、变压器、超声延迟线、大功率水声发射和接收、高压发生元件等。
CAS号：
性质：三种ABO3型化合物形成的三元系压电陶瓷固溶体为主晶相的陶瓷材料。它比二元系压电陶瓷如锆酸铅-钛酸铅（PBZrO3-PbTiO3）具有烧成温度范围宽、气孔率低等特性。在PBZrO3-PbTiO3二元系基础上加入的第三种成分的各种组合，称“复合金属离子组合”。常用的三元系压电陶瓷有：铌镁酸铅系[xPb(Mg1/3Nb2/3)O3-yPbTiO3-zPbZrO3]，铌锌酸铅系[xPb(Zn1/3Nb2/3)O3-yPbTiO3-zPbZrO3]，铌锰酸铅系[xPb(Mn1/3Nb2/3)O3-yPbTiO3-zPbZrO3]，铌锑酸铅系[xPb(Sb1/2Nb1/2)O3-yPbZrO3]，锑锰酸铅系[xPb(Mn1/3Sb2/3)O3-yPbTiO3-zPbZrO3]等。除用含铅化合物作为第三组元外，还有非铅化合物。如A+1B+5O32—或A+3B+3O32—等。三元系压电陶瓷类型很多。在三组元基础上，再加入第四种或更多种ABO3型化合物，则组成四元系或多元系压电陶瓷。其用途十分广泛。可用于制作扩音器、滤波器、变压器、超声延迟线、大功率水声发射和接收、高压发生元件等。