1) epoxy matrix
环氧树脂基体
1.
This article explains the reason of the implosion phenomenon in the production of epoxy matrix specialized in the hot-melt prepreg production.
分析了热熔法预浸料专用环氧树脂基体在制备中爆聚现象的原因,确定了采用先进的非电热加热树脂基体的方法和高低速多搅拌设备,用低活性的促进剂替代高活性促进剂,在70℃/30min的工艺条件下制备专用树脂,不仅有效控制树脂基体的爆聚,而且树脂基体的凝胶时间从6 min增长到13 mi n,延长了树脂基体及最终预浸料产品的贮存期。
2) epoxy resin matrix
环氧树脂基体
1.
An epoxy resin matrix with a grafting component used for modified PBO fiber was designed.
结合γ2射线辐照改性PBO纤维表面技术,将辐照介质(接枝体化合物)作为树脂基体的一个成分设计出环氧树脂基体配方。
3) Epoxy Resin Basal Body
环氧树脂基
1.
Containing Water Figuration Phase Change Material by Epoxy Resin Basal Body;
环氧树脂基含水定形相变材料
4) oil-base epoxy system
油基环氧树脂体系
5) epoxy matrix resin film
环氧树脂基树脂膜
1.
According to the requirements of low-temperature film forming property,high-temperature flowing property and impregnation property of epoxy matrix resin film used in RFI,a set of resin film preparation system which consists of GY6010 bisphenol A epoxy resin with high viscosity,HT907 HHPA and DY062 BDMA was designed.
据RFI工艺用环氧树脂基树脂膜低温成膜性、高温流动性和浸渗性的技术性能要求,设计了在一定温度内具有低反应活性的GY6010型高粘度液态双酚A二缩水甘油醚环氧树脂、HT907型六氢邻苯二甲酸酐和DY062型苄基二甲胺树脂膜制备体系。
6) fluorene-containing epoxy resin
芴基环氧树脂
补充资料：二氧化双环戊二烯环氧树脂
分子式：
CAS号：
性质：又称R型环氧树脂。双环戊二烯的二氧化物。白色结晶粉末，分子量164.2，相对密度1.330，熔融温度≥185℃，环氧当量82。易溶于乙酸、醇、醚、酮、苯、四氯化碳等。固化物马丁耐热200℃以上，耐候性及电性能好，硬度高，有自熄性。缺点是冲击性能欠佳。由双环戊二烯与过醋酸反应而得。可铸塑、模塑和层合。主要用作耐热、耐候铸塑料、模塑料、玻璃钢、胶黏剂和涂料。
CAS号：
性质：又称R型环氧树脂。双环戊二烯的二氧化物。白色结晶粉末，分子量164.2，相对密度1.330，熔融温度≥185℃，环氧当量82。易溶于乙酸、醇、醚、酮、苯、四氯化碳等。固化物马丁耐热200℃以上，耐候性及电性能好，硬度高，有自熄性。缺点是冲击性能欠佳。由双环戊二烯与过醋酸反应而得。可铸塑、模塑和层合。主要用作耐热、耐候铸塑料、模塑料、玻璃钢、胶黏剂和涂料。