1) Naphthol-based epoxy resin (NPER)
萘基环氧树脂(NPER)
2) Epoxy Resin Basal Body
环氧树脂基
1.
Containing Water Figuration Phase Change Material by Epoxy Resin Basal Body;
环氧树脂基含水定形相变材料
3) Bromine-containing naphthol formaldehyde epoxy resin
含溴萘酚酚醛环氧树脂
4) epoxy matrix resin film
环氧树脂基树脂膜
1.
According to the requirements of low-temperature film forming property,high-temperature flowing property and impregnation property of epoxy matrix resin film used in RFI,a set of resin film preparation system which consists of GY6010 bisphenol A epoxy resin with high viscosity,HT907 HHPA and DY062 BDMA was designed.
据RFI工艺用环氧树脂基树脂膜低温成膜性、高温流动性和浸渗性的技术性能要求,设计了在一定温度内具有低反应活性的GY6010型高粘度液态双酚A二缩水甘油醚环氧树脂、HT907型六氢邻苯二甲酸酐和DY062型苄基二甲胺树脂膜制备体系。
5) fluorene-containing epoxy resin
芴基环氧树脂
6) epoxy matrix
环氧树脂基体
1.
This article explains the reason of the implosion phenomenon in the production of epoxy matrix specialized in the hot-melt prepreg production.
分析了热熔法预浸料专用环氧树脂基体在制备中爆聚现象的原因,确定了采用先进的非电热加热树脂基体的方法和高低速多搅拌设备,用低活性的促进剂替代高活性促进剂,在70℃/30min的工艺条件下制备专用树脂,不仅有效控制树脂基体的爆聚,而且树脂基体的凝胶时间从6 min增长到13 mi n,延长了树脂基体及最终预浸料产品的贮存期。
补充资料：3-(6-甲氧基-2-萘基)-3-甲基环氧乙烷羧酸甲酯
分子式：C16H16O4
分子量：272.30
CAS号：56102-18-2
性质：结晶。熔点124-126℃。
制备方法：用β-萘酚在碱性条件下以硫酸二甲酯甲基化，生成β-甲氧基萘，然后在无水三氯化铝参与下与乙酸酐反应（乙酰化）得6-甲氧基-2-萘乙酮，将后者在甲醇钠参与下与氯乙酸甲酯缩合制得该品。
用途：萘普生的中间体。
分子量：272.30
CAS号：56102-18-2
性质：结晶。熔点124-126℃。
制备方法：用β-萘酚在碱性条件下以硫酸二甲酯甲基化，生成β-甲氧基萘，然后在无水三氯化铝参与下与乙酸酐反应（乙酰化）得6-甲氧基-2-萘乙酮，将后者在甲醇钠参与下与氯乙酸甲酯缩合制得该品。
用途：萘普生的中间体。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条