1)  oil-repellency finishing
拒油整理
2)  water and oil repellent agent
拒水拒油整理剂
3)  Water and Oil Repellent
拒水拒油整理
1.
Study on Water and Oil Repellent Finishing of Cotton Fabric by Use of Organic Fluorine and Modification with Antistatic Nano-Powder;
棉织物有机氟拒水拒油整理及纳米粉体抗静电改性研究
4)  oil repellent
拒油
1.
The Ploysulfonamide(PSA)fabric is finished by a water and oil repellent organic fluorine AG7600 and a cross-linking agent melamine formaldehyde resin.
采用含氟拒水拒油整理剂AG-7600,交联剂三聚氰胺甲醛对芳砜纶织物进行拒水拒油整理,经过试验,得到芳砜纶织物拒水拒油整理的最优工艺条件为AG-7600整理剂质量分数为6%、三聚氰胺甲醛交联剂质量分数为2%、焙烘温度为170℃、焙烘时间为1min,整理后织物获得良好的拒水拒油性能及耐久性。
5)  oil repellency
拒油
1.
The principles of textile water and oil repellency are discussed in the paper.
文章论述了纺织品的拒水拒油机理以及整理剂的选择,并应用纳米材料和有机氟树脂复配的整理剂对纯毛绒线进行了拒水拒油整理工艺的研究,采用经实验得到的整理优化工艺条件,对纯毛绒线进行整理,可赋予绒线优良的拒水拒油性能且具有耐久性,整理对后绒线的强力没有影响。
2.
The optimum process had been investigated and under the optimum process the water repellency,and oil repellency of the fabric were greatly improved.
文章论述了织物的拒水拒油机理以及拒水拒油整理剂的选择,采用纳米材料和有机氟树脂复配,利用正交试验设计实验方案对毛织物进行了拒水拒油整理,得到了提高毛织物的拒水拒油整理优化工艺条件,整理后的毛织物经AATCC-22和AATCC-11标准检测表明,具有优良的拒水拒油性和耐久性。
6)  Oil-repellent
拒油
1.
Water-and oil-repellent finishing of nylon-cotton union fabrics;
锦/棉交织物的拒水拒油整理
2.
This text analysed the shortcomings of traditional organic water-and-oil-repellent finishing, and researched the sol-gel method which developed the silicon dioxide water-and-oil-repellent finishing agent, and chosen the optimal relationship of all the reactants and activators and reaction conditions.
阐述了传统的有机拒水拒油整理的居多缺点,研究了溶胶凝胶法制备纳米二氧化硅拒水拒油整理剂的方法,得出各反应物和催化剂之间的最佳物质的量的比及反应条件。
参考词条
补充资料：拒油整理
    　　用拒油整理剂处理织物，在纤维上形成拒油表面的整理工艺过程。整理后织物的拒油表面张力低于各种油类的表面张力,使油在织物上成珠状而不易透入织物,从而产生拒油效果。经过拒油整理的织物，兼能拒水，并有良好的透气性。主要用于高级雨衣和特种服用材料。
　　
　　拒油整理剂一般为含有全氟烷基侧链的聚合物。下式所示的聚丙烯酸酯是一种良好的拒油整理剂。
　　
　　　
　　Rf=F3C(CF2)6～7，通常是7个或8个碳原子的全氟长链烷基，在纤维表面定向排列，使纤维具有拒油性，还可以?ü酋０返然藕捅┧嵯嗔Ｎ烁纳朴τ眯阅芎徒档统杀荆苡驼砑烈话闶怯珊榛牡ヌ搴鸵欢康谋┧狨サ鹊ヌ骞簿壑瞥伞Ｉ唐反蠖辔樽且海渲屑佑懈髦种烈允视Ω髦种锏男枰Ｕ淼囊话愎ひ帐墙渲频木苡驼砑寥樽且航?,烘干后在150℃左右焙烘3～4分钟，使其固着在纤维上，然后水洗。拒油整理剂可与多羟甲基三聚氰胺混用,能提高耐洗性,也可与拒水剂（见拒水整理）混用，以提高拒水性能。
　　
　　拒油整理效果的测试是以具有不同表面张力的正烷烃液体作为标准试液，分别滴在拒油整理后的织物上。根据成珠滴情况评定织物的拒油性能。表面张力小的试液能在织物上形成珠滴，即表明织物的拒油性能较好。
　　

说明：补充资料仅用于学习参考，请勿用于其它任何用途。