1) poly (phthalazinone ether sulfone ketone)
含二氮杂萘酮结构聚芳醚砜酮
1.
Blends of poly (phthalazinone ether sulfone ketone) (PPESK) and polytetrafluoroethylene (PTFE) were prepared via solution mixing, which was subjected to friction testing on a wear tester.
采用溶液共混法制备了不同质量比的新型含二氮杂萘酮结构聚芳醚砜酮(PPESK)与聚四氟乙烯(PTFE)共混物。
2) PPESK film
含二氮杂萘酮结构型聚醚砜酮膜
3) Poly(phthalazinone ether ketone ketone)
含二氮杂萘酮结构聚芳醚酮
1.
Poly(phthalazinone ether ketone ketone) (PPEKK),a novel high heat resistant performance thermoplastic,is an amorphous PAEK.
含二氮杂萘酮结构聚芳醚酮酮 (ＰＰＥＫＫ)是一种新型耐高温聚合物 ,相比于已经商品化的各种聚芳醚酮 ,ＰＰＥＫＫ除具有优异的综合性能外 ,它最大的特点表现在以下两方面 ,ＰＰＥＫＫ耐热性突出 ,玻璃化转变温度 (Ｔｇ)为 2 4 5℃左右 ,远高于各种商品化的聚芳醚酮 ;ＰＰＥＫＫ为无定型聚合物 ,易溶于多种有机极性溶剂 ,大大的扩展了材料的应用领域且丰富了成型手段[5] 。
4) Poly(phthalazinone ether ketone sulfone)
含二氮杂萘结构的聚醚砜酮
5) poly(phthalazinon ether sulfone) (PPES)
二氮杂萘酮聚芳醚砜(PPES)
6) sulfonated poly(phthalazinone ether ketone)
磺化二氮杂萘酮结构的聚醚酮
1.
Proton conductivity and methanol permeability of composite membranes based on sulfonated poly(phthalazinone ether ketone) doped with phosphotungstic acid;
磺化二氮杂萘酮结构的聚醚酮(SPPEK)与磷钨酸(PWA)的混合膜用两组分的DMAc混合溶液通过刮膜制备,对SPPEK/PWA膜进行了FTIR-ATR、表面形貌、质子导电性和甲醇透过性进行了研究。
补充资料：2-辛酮
结构式 CH3CO(CH2)5CH3
学名甲基正己基甲酮。无色液体。分子量128.21。密度0.8225-0.8255g/cm3。熔点-16℃。沸点175℃。闪点61℃。折射率1.4150-1.4165。不溶于水。能与醇和油混溶。以1:(9-12)溶于50％乙醇；以1:(1-1.7)溶于70％乙醇。具有类似未成熟苹果的水果香气及苦樟脑味。
生产方法：主要采用氧化法。以甲基己基甲醇为原料，在重铬酸钾和硫酸存在下，经氧化反应而得。也可以2-辛醇为原料，在氧化锌存在下，经氧化反应而得。
用途：酮类合成香料。主要用作薰衣草型香精的调合香料，以取代3-辛酮。也可用作木犀草、晚香玉、丁香、香石竹等香精的调合香料。还用于苹果、桃子等水果香精及干酪香精的调制。
学名甲基正己基甲酮。无色液体。分子量128.21。密度0.8225-0.8255g/cm3。熔点-16℃。沸点175℃。闪点61℃。折射率1.4150-1.4165。不溶于水。能与醇和油混溶。以1:(9-12)溶于50％乙醇；以1:(1-1.7)溶于70％乙醇。具有类似未成熟苹果的水果香气及苦樟脑味。
生产方法：主要采用氧化法。以甲基己基甲醇为原料，在重铬酸钾和硫酸存在下，经氧化反应而得。也可以2-辛醇为原料，在氧化锌存在下，经氧化反应而得。
用途：酮类合成香料。主要用作薰衣草型香精的调合香料，以取代3-辛酮。也可用作木犀草、晚香玉、丁香、香石竹等香精的调合香料。还用于苹果、桃子等水果香精及干酪香精的调制。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条