1) Al2O3/Al composite
Al2O3/Al复合材料
1.
The Al2O3/Al composite was fabricated by means of the pressureless infiltration technique of laying alloy on perform.
采用合金上置熔渗法制备Al2O3/Al复合材料,观测组织结构和相组成,分析助渗工艺及气氛的作用。
2) Al/Al2O3 composite
Al/Al2O3复合材料
1.
The microstructure of the prepared Al/Al2O3 composite cup shell was observed by SEM,and bend strength and fracture toughness of this alloy were measured.
对该工艺制备的Al/Al2O3复合材料杯形件进行扫描电镜观察、抗弯强度以及断裂韧性测量。
2.
An open cell porous Al and Al/Al2O3 composite were fabricated by powder sintering technique.
结果表明:Al/Al2O3复合材料有着比多孔铝更为有利的响应特征和更高的流动应力,该复合材料的压缩应力-应变曲线较为平坦,在与多孔铝相对密度相近时,屈服强度提高40%以上;经T6热处理,Al/Al2O3复合材料的屈服强度可进一步提高35%左右;此外,该复合材料的压缩行为具有明显的孔径依赖性,随孔径增大,流动应力升高,这主要与烧结过程中孔表面残留的气体有关。
3.
Microstructure observations showed that the amorphous Al2O3 nanolayers in the Al/Al2O3 composite were mostly destroyed after treating at 570℃ for 40 min.
观察了在不同温度下退火的Al/Al2O3复合材料的微观组织,结果表明,当退火温度达到570℃时包裹着Al核的非晶Al2O3壳开始破碎。
3) Al_2O_3/Ti-Al composites
Al2O3/Ti-Al复合材料
4) SiCp/Al2O3-Al composite
SiG/Al2O3-Al复合材料
5) A1_2O_3(sf)/A l composites
Al2O3(sf)/Al复合材料
6) Al2O3-SiC-Al composite
Al2O3-SiC-Al复合材料
1.
The effect Al-Mg alloy on the composition and microstructure of Al2O3-SiC-Al composite was investigated by SEM,EDS and XRD.
借助电子显微镜(SEM)、能谱(EDS)和X射线衍射(XRD)分析,研究铝镁合金对Al2O3-SiC-Al复合材料组成及微观结构的影响。
补充资料：silicon carbide whisker reinforced Al-matrix composite
分子式：
CAS号：
性质：以碳化硅晶须增强的铝基复合材料。碳化硅晶须(SiCw)为β晶型，直径约为0.05～2.0μm，长度10～200μm。这种复合材料的主要特点是：高比强、高比模。以20％SiC(质量)/2124Al复合材料为例，其室温拉伸强度可达800MPa，弹性模量为120GPa，比强度和比模量超过了钛合金；具有较好的中高温强度(使用温度可达300℃)；耐磨损、抗疲劳；热膨胀系数低，尺寸稳性好；具有良好的导电、导热性能；耐特殊环境，如放射线、高真空等；具有近似各向同性的性能，横向性能较高。主要缺点是塑性、断裂韧性较低，价格昂贵，其用途主要局限在航空、航天、军事等领域。
CAS号：
性质：以碳化硅晶须增强的铝基复合材料。碳化硅晶须(SiCw)为β晶型，直径约为0.05～2.0μm，长度10～200μm。这种复合材料的主要特点是：高比强、高比模。以20％SiC(质量)/2124Al复合材料为例，其室温拉伸强度可达800MPa，弹性模量为120GPa，比强度和比模量超过了钛合金；具有较好的中高温强度(使用温度可达300℃)；耐磨损、抗疲劳；热膨胀系数低，尺寸稳性好；具有良好的导电、导热性能；耐特殊环境，如放射线、高真空等；具有近似各向同性的性能，横向性能较高。主要缺点是塑性、断裂韧性较低，价格昂贵，其用途主要局限在航空、航天、军事等领域。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。