1) (Al 2O 3)p/(Al 4%Mg) matrix composites
(Al2O3)p/(Al-4wt.%Mg)复合材料
2) Al/Mg Laminated Composites
Al/Mg复合材料
1.
Dynamic Compressive Behavior of Al/Mg Laminated Composites and Its Influencing Factors;
结果表明,在约103s-1应变率时,Al/Mg层状金属复合材料应变率强化效应与动态热软化效应表现明显;随轧制压下率增大,材料流变应力降低;轧制温度对Al/Mg复合材料应力-应变曲线影响较大,流变应力变化规律不明显;轧后经300℃、1h退火后Al/Mg复合材料流变应力降低。
3) SiO2/Al-Mg composites
SiO2/Al-Mg复合材料
1.
Microstructure, phrase compositions and reaction processes of SiO2/Al-Mg composites fabricated by powdermetallurgy process have been studied.
对粉末冶金法制备的SiO2/Al-Mg复合材料的显微组织、物相组成及反应过程进行了研究,发现10%~20%SiO2-Al-Mg复合材料的最终物相均为MgAl2O4、MgO、Mg2Si、Si和Al。
4) Al/Al2O3 composite
Al/Al2O3复合材料
1.
The microstructure of the prepared Al/Al2O3 composite cup shell was observed by SEM,and bend strength and fracture toughness of this alloy were measured.
对该工艺制备的Al/Al2O3复合材料杯形件进行扫描电镜观察、抗弯强度以及断裂韧性测量。
2.
An open cell porous Al and Al/Al2O3 composite were fabricated by powder sintering technique.
结果表明:Al/Al2O3复合材料有着比多孔铝更为有利的响应特征和更高的流动应力,该复合材料的压缩应力-应变曲线较为平坦,在与多孔铝相对密度相近时,屈服强度提高40%以上;经T6热处理,Al/Al2O3复合材料的屈服强度可进一步提高35%左右;此外,该复合材料的压缩行为具有明显的孔径依赖性,随孔径增大,流动应力升高,这主要与烧结过程中孔表面残留的气体有关。
3.
Microstructure observations showed that the amorphous Al2O3 nanolayers in the Al/Al2O3 composite were mostly destroyed after treating at 570℃ for 40 min.
观察了在不同温度下退火的Al/Al2O3复合材料的微观组织,结果表明,当退火温度达到570℃时包裹着Al核的非晶Al2O3壳开始破碎。
5) Al2O3/Al composite
Al2O3/Al复合材料
1.
The Al2O3/Al composite was fabricated by means of the pressureless infiltration technique of laying alloy on perform.
采用合金上置熔渗法制备Al2O3/Al复合材料,观测组织结构和相组成,分析助渗工艺及气氛的作用。
6) Al_2O_3/Ti-Al composites
Al2O3/Ti-Al复合材料
补充资料：MG
分子式：
分子量：
CAS号：
性质：农药剂型的一种。细度介于颗粒剂和粉剂之间，粒度范围为60～200目，即297～74微米。能均匀分布在田间。既无粉剂那样易于飞扬扩大污染的缺点，又有颗粒体能延长残效的优点。使用方法与粉剂相同。
分子量：
CAS号：
性质：农药剂型的一种。细度介于颗粒剂和粉剂之间，粒度范围为60～200目，即297～74微米。能均匀分布在田间。既无粉剂那样易于飞扬扩大污染的缺点，又有颗粒体能延长残效的优点。使用方法与粉剂相同。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条