1) T2 copper plank
T2紫铜板材
1.
T2 copper plank after anneal is used as testing material.
以380℃×40min退火态的T2紫铜板材为研究对象, 板材按C路径6道次的连续剪切变形后,经分析表明:连续剪切变形后的板材的显微组织明显得到细化,并且呈现出剪切流线形态;变形后的板材的抗拉强度由退火态的210MPa提高到330MPa;硬度从65HV1提高到120HV1。
2) T2 copper foil
T2紫铜箔
1.
In this paper, the influences of specimen thickness and the size of crystal grain on mechanical properties of micro specimen of T2 copper foil are studied, the thickness of 100μm, 80μm and 60μm were selected with the heat treatment temperature of 400℃, 500℃, 600℃and 700℃, and the tensile speed is 0.
本文通过拉伸实验研究了T2紫铜箔微小试样的厚度和晶粒尺寸对力学性能的影响规律,选取的箔材厚度分别为100μm、80μm、60μm和40μm,热处理温度分别为400℃、500℃、600℃和700℃,拉伸速度为0。
3) T2 copper/10 steel
T2紫铜/10#钢
4) red copper bar
紫铜棒材
1.
Features of fractured surface and microstructure ofplastic shearing zone of red copper bar under axial load;
紫铜棒材轴向加压精密塑性剪切变形区的金相组织和断面特征