1) T2 copper
T2纯铜
1.
Two sequences of tension-fatigue and fatigue-tension were performed on T2 copper and brass H62 sheet.
本文以T2纯铜和H62黄铜为研究对象，进行拉伸—疲劳和疲劳—拉伸两种接续加载，两接续加载轴之间夹角Φ选取两个典型值(0°和45°)。
2) T_2 pure copper strip
T2纯铜带
3) T2 copper foil
T2紫铜箔
1.
In this paper, the influences of specimen thickness and the size of crystal grain on mechanical properties of micro specimen of T2 copper foil are studied, the thickness of 100μm, 80μm and 60μm were selected with the heat treatment temperature of 400℃, 500℃, 600℃and 700℃, and the tensile speed is 0.
本文通过拉伸实验研究了T2紫铜箔微小试样的厚度和晶粒尺寸对力学性能的影响规律,选取的箔材厚度分别为100μm、80μm、60μm和40μm,热处理温度分别为400℃、500℃、600℃和700℃,拉伸速度为0。
4) T2 copper plank
T2紫铜板材
1.
T2 copper plank after anneal is used as testing material.
以380℃×40min退火态的T2紫铜板材为研究对象, 板材按C路径6道次的连续剪切变形后,经分析表明:连续剪切变形后的板材的显微组织明显得到细化,并且呈现出剪切流线形态;变形后的板材的抗拉强度由退火态的210MPa提高到330MPa;硬度从65HV1提高到120HV1。
5) T2 copper/10 steel
T2紫铜/10#钢
6) T_2
T2
1.
Currently CPMG T_2 logging in all wireline NMR logging tools has been the industry standard.
在电缆核磁共振(NMR)测井中,CPMGT2回波串测量已成为NMR测井的工业标准。
2.
The application of T_2 to the polymerization and other abnormal conditions is described.
论述了T2在聚合反应和其它异常情况的应用,通过对比研究,得出了其因果关系,在生产中起到了较好的效果。
补充资料：纯铜
分子式：
CAS号：
性质：工业用金属铜，纯度高于99.5%，呈紫红色，又称纯铜。它具有优良的导电、导热、耐蚀和焊接性能，在室温下的导电性能仅次于银。一般分三类：(1)加工紫铜，其中又分四种牌号，即一号、二号、三号和四号紫铜，纯度分别为99.95%，99.90%，99.70%和99.5%；(2)无氧铜和脱氧铜。无氧铜有一号和二号两种，含氧量均小于0.003%，脱氧铜分磷脱氧铜和锰脱氧铜两种，含氧量小于0.001%，磷的残留量0.01%～0.04%，锰的残留量0.1%～0.3%；(3)特种铜，有砷铜、银铜、碲铜三种，砷、碲含量均为0.5%，银含量为0.03%～0.25%，这些铜除了高导电性以外，还具备一些特殊性能，如碲改善铜的切削性能，砷改善含氧铜的加工性能和耐蚀性能，提高再结晶软化温度和抗蠕变强度。
CAS号：
性质：工业用金属铜，纯度高于99.5%，呈紫红色，又称纯铜。它具有优良的导电、导热、耐蚀和焊接性能，在室温下的导电性能仅次于银。一般分三类：(1)加工紫铜，其中又分四种牌号，即一号、二号、三号和四号紫铜，纯度分别为99.95%，99.90%，99.70%和99.5%；(2)无氧铜和脱氧铜。无氧铜有一号和二号两种，含氧量均小于0.003%，脱氧铜分磷脱氧铜和锰脱氧铜两种，含氧量小于0.001%，磷的残留量0.01%～0.04%，锰的残留量0.1%～0.3%；(3)特种铜，有砷铜、银铜、碲铜三种，砷、碲含量均为0.5%，银含量为0.03%～0.25%，这些铜除了高导电性以外，还具备一些特殊性能，如碲改善铜的切削性能，砷改善含氧铜的加工性能和耐蚀性能，提高再结晶软化温度和抗蠕变强度。