1) Magnesium methacrylate
甲基丙烯酸镁
1.
Reinforcement of magnesium methacrylate prepared in situ to natural rubber;
原位生成甲基丙烯酸镁补强天然橡胶的研究(英文)
2.
Effect of magnesium methacrylate on properties of EVM vulcanizate;
甲基丙烯酸镁对EVM硫化胶性能的影响
3.
Metal salt of unsaturated carboxylic acid, such as magnesium methacrylate [(Mg(MAA) 2] shows a great reinforcing effect on peroxide cured nitrile rubber (NBR).
甲基丙烯酸镁 (Mg(MAA) 2 )等不饱和羧酸金属盐在过氧化物硫化体系下对丁腈橡胶(NBR)有明显的补强作用 。
2) magnesium dimethacrylate
甲基丙烯酸镁
1.
Ethylene -vinyl acetate copolymer was blended with magnesium dimethacrylate(MDMA)and cured by perox-ide.
将甲基丙烯酸镁(MDMA)直接与乙烯-乙酸乙烯共聚物(EVM)共混,并用过氧化物硫化,研究了过氧化二异丙苯(DCP)和MDMA用量对EVM硫化胶物理机械性能和交联结构的影响。
2.
The preparation, structure and properties of halogen free flame retardant ethylene propylene diene monomer (EPDM) highly filled with magnesium hydroxide (Mg(OH)2) with the addition of magnesium dimethacrylate (MDMA) and halogen free flame retardant EPDM based on silicone rubber and MDMA were studied in this paper.
本论文采用加入甲基丙烯酸镁(MDMA)的方法来制备具有优良力学性能的高填充氢氧化镁(Mg(OH)2)的三元乙丙橡胶(EPDM)和采用以硅橡胶(MVQ)、甲基丙烯酸镁(MDMA)为阻燃体系制备的无卤阻燃三元乙丙橡胶(EPDM)。
3) magnesium acrylate
丙烯酸镁
1.
Under the peroxide vulcanizing system,the reinforcements of magnesium acrylate prepared by magnesium oxide and acrylic acid in-situ on natural rubber were studied.
研究了在过氧化硫化体系条件下,通过氧化镁(MgO)和丙烯酸(AA)原位生成丙烯酸镁[Mg(AA)2]对NR的补强作用。
4) methyl acrylic acid
甲基丙烯酸
1.
Study on the Catalyst Used in Direct Oxidation of Isobutane to Methyl Acrylic Acid;
异丁烷直接氧化制甲基丙烯酸催化剂的研究
2.
A new polymeric surfactant using for acrylic acid waterborne coatings was prepared from the methyl acrylic acid,styrene,hydroxyethyl acrylate and 2-ethylhexyl acrylate.
以甲基丙烯酸、苯乙烯、丙烯酸羟乙酯和丙烯酸-2-乙基己酯为主要原料,通过溶液共聚法合成了用于丙烯酸酯水性涂料的高分子表面活性剂。
3.
Polypropylene (PP) was swelled with a solution of methyl acrylic acid (MAA) in supercritical CO2 and was grafted with MAA via free radical polymerization leading to PP-g-MAA, with a maximum grafting degree of 14.
利用超临界CO2作为甲基丙烯酸(MAA)的溶剂和聚丙烯(PP)的溶胀剂,合成了MAA与PP的接枝聚合物 (PP-g-MAA)。
5) methacrylic acid
甲基丙烯酸
1.
Surface Organic Modification of Hydroxypatite Particles through UV Irradiation Polymerization of Methacrylic Acid;
羟基磷灰石表面光引发甲基丙烯酸聚合有机化改性的研究
2.
Ethylene-propylene-diene rubber filled with nano-calcium carbonate in-situ modified by methacrylic acid Ⅰ.Effect of curing agent and methacrylic acid amount;
用甲基丙烯酸原位改性纳米碳酸钙填充三元乙丙橡胶 Ⅰ.交联剂和甲基丙烯酸用量的影响
3.
Ethylene-propylene-diene rubber filled with nano-CaCO_3 in-situ modified by methacrylic acid Ⅱ. Effect of nano-CaCO_3 amount;
用甲基丙烯酸原位改性纳米CaCO_3填充三元乙丙橡胶 Ⅱ.纳米CaCO_3用量的影响
6) methacylic acid
甲基丙烯酸
1.
Acrylonitrile(AN)/ methacylic acid(MAA) copolymer foam plastic was prepared by free foaming.
通过烘箱自由发泡制备丙烯腈(AN)/甲基丙烯酸(MAA)共聚物泡沫塑料,讨论了该泡沫塑料泡孔平均孔径随泡沫塑料密度变化的规律,研究了成核剂和应力对泡沫塑料泡孔尺寸的影响,通过光学显微和电子扫描显微观察了该泡沫塑料的整体结构和微观结构。
2.
Copolymer foam of acrylonitrile (AN)/methacylic acid (MAA) was prepared and characterized using optical microscope, inf rared adsorption spectrum and differential thermal analysis (DSC).
研究了丙烯腈(AN)／甲基丙烯酸(MAA)共聚物泡沫塑料的合成配方和制备该泡沫塑料的方法,对该泡沫塑料进行了光学显微镜、红外光谱和差示扫描量热法分析。
3.
Acrylonitrile (AN)/ methacylic acid (MAA) copolymer foam plastic was prepared by two-step production.
本论文以二步法制备了丙烯腈(AN)/甲基丙烯酸(MAA)共聚物泡沫塑料。
补充资料：甲基丙烯酸甲酯、甲基丙烯酸丁酯、甲基丙烯酸的聚合物
CAS：28262-63-7
分子式：(C8H14O2·C5H8O2·C4H6O2)x
中文名称：2-甲基-2-丙烯酸与2-甲基-2-丙烯酸丁酯和2-甲基-2-丙烯酸甲酯的聚合物
甲基丙烯酸甲酯、甲基丙烯酸丁酯、甲基丙烯酸的聚合物
英文名称：2-Propenoic acid, 2-methyl-, polymer with butyl 2-methyl-2-propenoate and methyl 2-methyl-2-propenoate
Butyl methacrylate, methyl methacrylate, methacrylic acid polymer
分子式：(C8H14O2·C5H8O2·C4H6O2)x
中文名称：2-甲基-2-丙烯酸与2-甲基-2-丙烯酸丁酯和2-甲基-2-丙烯酸甲酯的聚合物
甲基丙烯酸甲酯、甲基丙烯酸丁酯、甲基丙烯酸的聚合物
英文名称：2-Propenoic acid, 2-methyl-, polymer with butyl 2-methyl-2-propenoate and methyl 2-methyl-2-propenoate
Butyl methacrylate, methyl methacrylate, methacrylic acid polymer