1) sulfone-polyetheramide(PEA)
含砜聚醚酰胺(PEA)
2) polyarylene sulfide sulfone amide
聚芳硫醚砜酰胺
1.
Diamine monomer containing sulfide was synthesized firstly,then polyarylene sulfide sulfone amide(PASSA)with high molecular weight was synthesized at low temperature.
与以往的以硫化钠为硫源采用高温聚合合成聚芳硫醚类树脂的方法不同,采用先合成含硫醚键的单体,然后进行低温溶液缩聚,合成了高分子量的新型聚芳硫醚砜酰胺(PASSA)树脂,其特性粘度可达到0。
2.
Diamine monomers containing sulfone or ketone group were synthesized firstly,then polyarylene sulfide sulfone amide(PASSA) and polyarylene sulfide ketone amide(PASKA) with high molecular weight were synthesized by a low temperature polycondensation reaction in anhydrous N-methylpyrrolidone (NMP).
采用先合成含硫醚键的单体,后进行低温溶液缩聚的方法,合成高分子量的新型聚芳硫醚酰胺类树脂——聚芳硫醚砜酰胺(PASSA)和聚芳硫醚酮酰胺(PASKA),其特性粘数分别为0。
3) poly(aryl oxide sulfone-imide)
聚芳醚砜酰亚胺
5) zinc-containing poly(ether ester amide)
含锌聚醚酯酰胺
1.
Thermal property of zinc-containing poly(ether ester amide)
含锌聚醚酯酰胺的热性能研究
6) polyarylene sulfide sulfone imide
聚芳硫醚砜酰亚胺
1.
A novel heat-resistant material polyarylene sulfide sulfone imide (PASSI) was synthesized successfully.
用化学酰亚胺技术首先合成含完全酰亚胺环的单体,然后与Na2S常压聚合,从而在聚芳硫醚分子主链中引入了刚性的酰亚胺环,合成聚芳硫醚砜酰亚胺(PASSI),并对单体及聚合物进行表征,通过热分析得出聚合物的玻璃化温度为252。
补充资料：PEA
分子式：C8H11NO
分子量：137.18
CAS号：122-98-5
性质：无色液体。熔点-30℃，沸点268℃，167℃（2.27kPa），相对密度1.085。微溶于水，易溶于乙醇、乙醚、氯仿。
制备方法：将46.5g（0.5mol）苯胺、20g（0.25mol）氯乙酸和50ml水混合，加热回流3h。然后用碳酰钠溶液碱化，用水蒸出过量的苯胺，将剩余物减压蒸馏，收集161-163℃（2.13kPa）馏分，得N-羟乙基苯胺22-24g，收率64-70%。
用途：有机合成中间体。
分子量：137.18
CAS号：122-98-5
性质：无色液体。熔点-30℃，沸点268℃，167℃（2.27kPa），相对密度1.085。微溶于水，易溶于乙醇、乙醚、氯仿。
制备方法：将46.5g（0.5mol）苯胺、20g（0.25mol）氯乙酸和50ml水混合，加热回流3h。然后用碳酰钠溶液碱化，用水蒸出过量的苯胺，将剩余物减压蒸馏，收集161-163℃（2.13kPa）馏分，得N-羟乙基苯胺22-24g，收率64-70%。
用途：有机合成中间体。