1) Ni/Al powder
Ni/Al
1.
The analysis results show that this method can prepare the compact shell for Ni/Al powder.
在含氟离子的水溶液中,采用Al粉直接置换还原Ni盐的方法,实现了纳米Ni在Al粉表面上的快速化学沉积,制备出核-壳结构的Ni/Al复合粉末。
2) Ni-Al based
Ni-Al基
3) Al/Ni coating
Al/Ni涂层
4) Ni-Al alloy
Ni-Al合金
1.
Phase formation regularities of Ni-Al alloy nano powders prepared by vapor deposition;
气相沉积制备Ni-Al合金纳米粉末的相生成规律
2.
Based on the microscopic phase-field dynamic model and the microelasticity theory, the morphology evolution of Ni_3Al(γ′)phase and early precipitation mechanism in Ni-Al alloy were simulated.
基于微观相场动力学模型和微观弹性能理论,对Ni-Al合金中沉淀相Ni_3Al(γ′)形貌演化、早期沉淀机制和后期粗化过程进行了原子层面的计算机模拟。
3.
Based on the microscopic phase-field dynamic model and the microelasticity theory, the morphology evolution and early precipitation mechanism of γ precipitated phase of Ni-Al alloy is studied at atomic-scale.
基于离散格点形式的微观扩散方程和微观弹性能理论,对Ni-Al合金沉淀过程中γ’相(Ni3Al)的沉淀相形貌和早期沉淀机制进行了原子层面计算机模拟。
5) Al-Ni alloy
Al-Ni合金
1.
Effects of high magnetic field on solidification structure of Al_3Ni phase in Al-Ni alloy;
强磁场下Al-Ni合金凝固初生相Al_3Ni的取向行为
6) Al/Ni-ZrO2
Al/Ni-ZrO_2
补充资料:Ni-Al microwave ferrite
分子式:Ni-Al
CAS号:
性质:又称镍-铝微波铁氧体。在镍旋磁铁氧体基础上,用三价铝离子置换一部分三价铁离子形成的镍-铝旋磁铁氧体。化学式为NiAlxFe2-xO4。当Alx的x值达约0.7%,磁性出现反常现象,这时材料已无实用值。按铝含量而分为0.1≤x≤0.4和0.7≤x≤1.0两类旋磁铁氧体。饱和磁化强度0.035~0.145T,随铝量换量的增加而降低。居里温度155~440℃。铁磁共振线宽18.0~44.0kA/m(9kHz)。介电常数8.2~9.5。介质损耗角正切值(3~50)×10-4。采用电子陶瓷工艺,热压烧结或氮气氛烧结。适于制作高功率器件。
CAS号:
性质:又称镍-铝微波铁氧体。在镍旋磁铁氧体基础上,用三价铝离子置换一部分三价铁离子形成的镍-铝旋磁铁氧体。化学式为NiAlxFe2-xO4。当Alx的x值达约0.7%,磁性出现反常现象,这时材料已无实用值。按铝含量而分为0.1≤x≤0.4和0.7≤x≤1.0两类旋磁铁氧体。饱和磁化强度0.035~0.145T,随铝量换量的增加而降低。居里温度155~440℃。铁磁共振线宽18.0~44.0kA/m(9kHz)。介电常数8.2~9.5。介质损耗角正切值(3~50)×10-4。采用电子陶瓷工艺,热压烧结或氮气氛烧结。适于制作高功率器件。
说明:补充资料仅用于学习参考,请勿用于其它任何用途。