1) inorganic adhesive
无机胶粘剂
1.
In this paper,the types,the characteristics and the applications of inorganic adhesives were introduced in detail.
详细介绍了无机胶粘剂的种类、特性、应用范围。
2) Cu-Al inorganic adhesive
铜-铝无机胶粘剂
3) silicate inorganic adhesive
硅酸盐无机胶粘剂
1.
Preparation and application of the silicate inorganic adhesive;
硅酸盐无机胶粘剂的研制及应用
2.
In order to research the mechanisms of solidification of silicate inorganic adhesive,the moisture evaporation law in solidification process of the adhesive and its solidification kinetics was investigated based on the experiment in which the dehydration rate in solidification process was determined.
为了探讨硅酸盐无机胶粘剂的固化机理,通过硅酸盐无机胶粘剂固化过程中水份蒸发速率的测定,分析了其固化过程中的失水规律和动力学特征。
4) non-formaldehyde adhesive
无醛胶粘剂
1.
In this work,a non-formaldehyde adhesive for plywood was prepared.
本研究以水性异氰酸酯为交联剂,以聚乙烯醇、橡胶乳液与各助剂共混为主剂,制成了环保型人造板用无醛胶粘剂。
5) non solvent adhesive
无溶剂胶粘剂
6) inorganic binding material
无机粘结胶
1.
Performances of inorganic binding material and its application —an ideal material for remedying and reinforcing concrete works;
一种用于混凝土修补的无机粘结胶的性能及应用
补充资料：无机胶粘剂
由无机物制成的胶粘剂,也称无机胶。广义地讲,硅酸钠、矿渣水泥、硫磺、石膏等古老的无机粘接材料也属无机胶范畴；狭义地讲,通常多指磷酸锌-硅酸盐、氧化铜-磷酸,耐热硅酸盐等反应型无机胶。其中,氧化铜-磷酸无机胶的配制和使用方法是：在磷酸溶液（加有氢氧化铝）中，按比例加入特制的氧化铜粉,混合均匀,涂刷在经粗化的粘接面上，胶层由于氧化铜、磷酸、磷酸铝之间的化学反应而固化，形成牢固的粘接接头。
无机胶主要用于金属、玻璃、陶瓷等无机材料的粘接。无机胶的耐热性、不燃性、耐久性及耐油性比有机胶好得多。无机胶可在 400～1300°C下工作。但其耐碱性能较差，性脆，其粘接接头不耐冲击、剥离和疲劳。采用套接(图1)和嵌接接头（图2）可以克服无机胶性脆及平面粘接强度低的缺点。如氧化铜－磷酸无机胶用于钢质的轴与孔的套接时，压缩剪切强度达100MPa。无机胶已成功地用于火箭、导弹以及常用的燃烧器的耐热部件的粘接；用于加热设备的陶瓷和金属部件的装配固定；也广泛用于各种刀具、量具、管轴等零部件的粘接与修复。
无机胶主要用于金属、玻璃、陶瓷等无机材料的粘接。无机胶的耐热性、不燃性、耐久性及耐油性比有机胶好得多。无机胶可在 400～1300°C下工作。但其耐碱性能较差，性脆，其粘接接头不耐冲击、剥离和疲劳。采用套接(图1)和嵌接接头（图2）可以克服无机胶性脆及平面粘接强度低的缺点。如氧化铜－磷酸无机胶用于钢质的轴与孔的套接时，压缩剪切强度达100MPa。无机胶已成功地用于火箭、导弹以及常用的燃烧器的耐热部件的粘接；用于加热设备的陶瓷和金属部件的装配固定；也广泛用于各种刀具、量具、管轴等零部件的粘接与修复。