1) mineral binder hond
无机粘洁剂
2) inorganic adhesive
无机胶粘剂
1.
In this paper,the types,the characteristics and the applications of inorganic adhesives were introduced in detail.
详细介绍了无机胶粘剂的种类、特性、应用范围。
3) inorganic binder
无机粘结剂
1.
The composite inorganic electric heating carbon coating was prepared by adding composite carbon powders as conductive filler into inorganic binder,coating molded onto the surface of the heat resisting matrix after .
采用在耐热无机粘结剂中添加复合型炭系粉料,在耐热载体表面预埋电极后用涂覆法成型固化,再在其表面喷涂含铝高温涂料经二次固化制得复合型无机炭系电热涂层。
2.
The title organic-inorganic hybrid heat resistant insulation coatings has been developed based on organic resin, inorganic binder and fillers, which shows good adhesion and insulation properties after heat treatment at 600℃ 1h.
采用有机硅树脂、无机粘结剂和无机填料制备的有机无机复合耐高温绝缘漆,其涂层经600℃,1h的热处理后可具有良好的附着力和绝缘性能。
5) inorganic viscose
无机粘结剂
1.
Based a vast amount of upon tests,we use an inorganic viscose——Nami viscose in the smearing powder techology for the compact fluorescent lamp tube to replace the organic viscose,such as nitrocotton in the traditional smearing techology.
在大量试验的基础上，在双Ｕ紧凑型荧光灯管的涂粉工艺中采用无机粘结剂——纳米胶，取代传统涂粉工艺中的有机粘结剂（硝化棉），用水溶剂（去离子水或蒸馏水）代替醋酸丁酯溶剂，免去了高温烤管工艺，得到了粘着强度牢固、涂层厚度适宜、外观洁白的紧凑型荧光灯。
6) inorganic bond
无机粘合剂
补充资料：无机胶粘剂
由无机物制成的胶粘剂,也称无机胶。广义地讲,硅酸钠、矿渣水泥、硫磺、石膏等古老的无机粘接材料也属无机胶范畴；狭义地讲,通常多指磷酸锌-硅酸盐、氧化铜-磷酸,耐热硅酸盐等反应型无机胶。其中,氧化铜-磷酸无机胶的配制和使用方法是：在磷酸溶液（加有氢氧化铝）中，按比例加入特制的氧化铜粉,混合均匀,涂刷在经粗化的粘接面上，胶层由于氧化铜、磷酸、磷酸铝之间的化学反应而固化，形成牢固的粘接接头。
无机胶主要用于金属、玻璃、陶瓷等无机材料的粘接。无机胶的耐热性、不燃性、耐久性及耐油性比有机胶好得多。无机胶可在 400～1300°C下工作。但其耐碱性能较差，性脆，其粘接接头不耐冲击、剥离和疲劳。采用套接(图1)和嵌接接头（图2）可以克服无机胶性脆及平面粘接强度低的缺点。如氧化铜－磷酸无机胶用于钢质的轴与孔的套接时，压缩剪切强度达100MPa。无机胶已成功地用于火箭、导弹以及常用的燃烧器的耐热部件的粘接；用于加热设备的陶瓷和金属部件的装配固定；也广泛用于各种刀具、量具、管轴等零部件的粘接与修复。
无机胶主要用于金属、玻璃、陶瓷等无机材料的粘接。无机胶的耐热性、不燃性、耐久性及耐油性比有机胶好得多。无机胶可在 400～1300°C下工作。但其耐碱性能较差，性脆，其粘接接头不耐冲击、剥离和疲劳。采用套接(图1)和嵌接接头（图2）可以克服无机胶性脆及平面粘接强度低的缺点。如氧化铜－磷酸无机胶用于钢质的轴与孔的套接时，压缩剪切强度达100MPa。无机胶已成功地用于火箭、导弹以及常用的燃烧器的耐热部件的粘接；用于加热设备的陶瓷和金属部件的装配固定；也广泛用于各种刀具、量具、管轴等零部件的粘接与修复。