1) alkali-activated phosphorous slag cement
碱磷渣水泥
2) phosphorous slag cement
磷渣水泥
1.
The hydration products of clinker poor phosphorous slag cement were analyzed and identified by means of XRD, SEM and DTA.
利用Ｘ射线衍射、扫描电镜及差热分析等测试手段，对少熟料磷渣水泥的水化产物进行了分析，并结合三甲基硅烷化法和压汞仪对该种水泥的水化硬化过程进行了研究。
3) alkali-activated slag cement
碱矿渣水泥
1.
Experimental study and technical analysis of 32.5 alkali-activated slag cement;
32.5碱矿渣水泥的试验研究与技术分析
2.
Study on large volume poured alkali-activated slag cement based on low and intermediate level radioactive waste;
大体积浇注碱矿渣水泥中低放废液固化研究
3.
Adsorption characteristics of surfactant in alkali-activated slag cement systems
表面活性剂在碱矿渣水泥系统中的吸附特征研究
4) alkali slag cement
碱矿渣水泥
1.
Development of class 32.5 alkali slag cement;
32.5级碱矿渣水泥的研制
2.
Study onlight wall partition with alkali slag cement-red soil base;
碱矿渣水泥-赤泥基轻质隔墙板的研究
3.
The study shows that the alkali slag cement ground from the mixture of slag, solid alkali ex citant and additive in certain proportion can be above 60 Mpa for its 28 - day strength and of normal setting time.
研究表明：将矿渣、固体碱性激发剂、外加剂三种原料按一定配比混合入唐进行粉磨，制备得到的减矿渣水泥28d强度达到60MPa以上，凝结时间正常；这种碱矿渣水泥生产成本低、性能优良，是一种具有发展前景的新型水泥。
5) alkali activated slag cement
碱矿渣水泥
1.
Research on chemical shrinkage of alkali activated slag cement;
碱矿渣水泥化学收缩研究
2.
This paper discussed the use of alkali activated slag cement (AASC)to solidify high level radioactive waste liquid,combining with present research situation of internal and external.
从这三个方面出发，通过对碱矿渣水泥固化高放废液的研究，并结合国内外水泥固化高放废液的研究现状，初步分析和阐述了碱矿渣水泥固化高放废液的理论依据，指出碱矿渣水泥比硅酸盐水泥更适用于高放废液的固化。
3.
This paper is specialized in the free sintering brick based alkali activated slag cement,red mud and fly ash Making use of different activators A and B,the optimum proportional of various materials which constitute the brick is researched The results show that the grade of the brick,under the condition of the optimum proportional,can reach 20 leve
主要对利用碱矿渣水泥、赤泥和粉煤灰等材料制造免烧砖的技术进行了研究，使用了不同的激发剂 Ａ 和 Ｂ，并确定了各组分材料的最佳配比。
6) alkali-slag cement
碱矿渣水泥
1.
Low dosage and high performance retarder with the function of grinding aid was developed on the basis of the hydration mechanism of alkali－ slag cement.
根据碱矿渣水泥水化机理，研制出兼有助磨作用的低掺量高效缓凝剂。
2.
In this paper,the influence of set- retarding on applications of alkali- slag cement and concrete is analysed.
本文分析了缓凝问题对碱矿渣水泥及混凝土应用的影响；讨论了碱矿渣水泥的凝结特点及现有缓凝措施的适用性，认为掺用有效的缓凝剂才是解决该胶凝材料系统易于出现速凝现象的根本途径；有关缓凝剂作用机理及新型复合缓凝剂的研究仍是碱矿渣水泥及混凝土研究领域的重要课
补充资料：磷渣水泥
分子式：
分子量：
CAS号：
性质：由硅酸盐水泥熟料、粒化电炉磷渣和适量石膏磨细制成的水硬性胶凝材料。水泥中磷渣掺加量为20％～40％。按强度等级分为325、425、525三个标号。使用范围与矿渣硅酸盐水泥相同。
分子量：
CAS号：
性质：由硅酸盐水泥熟料、粒化电炉磷渣和适量石膏磨细制成的水硬性胶凝材料。水泥中磷渣掺加量为20％～40％。按强度等级分为325、425、525三个标号。使用范围与矿渣硅酸盐水泥相同。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。