1) alkali-activated slag cement mortars
碱矿渣水泥砂浆
1.
The carbonation depth of alkali-activated slag cement mortars decreases with content of alkali equivalent increasing in the range of 3% to 6%.
研究了碱当量(以氧化钠当量计)、水胶比和胶砂比对碱矿渣水泥砂浆抗碳化性能的影响,并与硅酸盐水泥砂浆进行了对比试验。
2) alkali-activated slag cement
碱矿渣水泥
1.
Experimental study and technical analysis of 32.5 alkali-activated slag cement;
32.5碱矿渣水泥的试验研究与技术分析
2.
Study on large volume poured alkali-activated slag cement based on low and intermediate level radioactive waste;
大体积浇注碱矿渣水泥中低放废液固化研究
3.
Adsorption characteristics of surfactant in alkali-activated slag cement systems
表面活性剂在碱矿渣水泥系统中的吸附特征研究
3) alkali slag cement
碱矿渣水泥
1.
Development of class 32.5 alkali slag cement;
32.5级碱矿渣水泥的研制
2.
Study onlight wall partition with alkali slag cement-red soil base;
碱矿渣水泥-赤泥基轻质隔墙板的研究
3.
The study shows that the alkali slag cement ground from the mixture of slag, solid alkali ex citant and additive in certain proportion can be above 60 Mpa for its 28 - day strength and of normal setting time.
研究表明：将矿渣、固体碱性激发剂、外加剂三种原料按一定配比混合入唐进行粉磨，制备得到的减矿渣水泥28d强度达到60MPa以上，凝结时间正常；这种碱矿渣水泥生产成本低、性能优良，是一种具有发展前景的新型水泥。
4) alkali activated slag cement
碱矿渣水泥
1.
Research on chemical shrinkage of alkali activated slag cement;
碱矿渣水泥化学收缩研究
2.
This paper discussed the use of alkali activated slag cement (AASC)to solidify high level radioactive waste liquid,combining with present research situation of internal and external.
从这三个方面出发，通过对碱矿渣水泥固化高放废液的研究，并结合国内外水泥固化高放废液的研究现状，初步分析和阐述了碱矿渣水泥固化高放废液的理论依据，指出碱矿渣水泥比硅酸盐水泥更适用于高放废液的固化。
3.
This paper is specialized in the free sintering brick based alkali activated slag cement,red mud and fly ash Making use of different activators A and B,the optimum proportional of various materials which constitute the brick is researched The results show that the grade of the brick,under the condition of the optimum proportional,can reach 20 leve
主要对利用碱矿渣水泥、赤泥和粉煤灰等材料制造免烧砖的技术进行了研究，使用了不同的激发剂 Ａ 和 Ｂ，并确定了各组分材料的最佳配比。
5) alkali-slag cement
碱矿渣水泥
1.
Low dosage and high performance retarder with the function of grinding aid was developed on the basis of the hydration mechanism of alkali－ slag cement.
根据碱矿渣水泥水化机理，研制出兼有助磨作用的低掺量高效缓凝剂。
2.
In this paper,the influence of set- retarding on applications of alkali- slag cement and concrete is analysed.
本文分析了缓凝问题对碱矿渣水泥及混凝土应用的影响；讨论了碱矿渣水泥的凝结特点及现有缓凝措施的适用性，认为掺用有效的缓凝剂才是解决该胶凝材料系统易于出现速凝现象的根本途径；有关缓凝剂作用机理及新型复合缓凝剂的研究仍是碱矿渣水泥及混凝土研究领域的重要课
6) alkali slag cement
碱-矿渣水泥
补充资料：矿渣水泥
分子式：
CAS号：
性质：由硅酸盐水泥熟料加入适量石膏的同时，加人20％～70％的粒化高炉矿渣共同磨细制成的水硬性胶凝材料。简称为矿渣水泥，代号为P·S。有275，325，425，525，625五个标号以及425R，525R两种早强型水泥。矿渣水泥密度为2.8～3.1g/cm3，需水量较少，保水性和抗冻性差。由于减少了熟料，水化热变低，而抗硫酸盐腐蚀能力提高。不宜用于冬季施工和要求早期强度较高的工程，适于高湿度环境和长期处于水下的工程。在28天后强度有可能继续增长而超过普通硅酸盐水泥。用矿渣水泥的混凝土易泌水而不易振捣密实，不宜用于有较高抗渗要求的混凝土。
CAS号：
性质：由硅酸盐水泥熟料加入适量石膏的同时，加人20％～70％的粒化高炉矿渣共同磨细制成的水硬性胶凝材料。简称为矿渣水泥，代号为P·S。有275，325，425，525，625五个标号以及425R，525R两种早强型水泥。矿渣水泥密度为2.8～3.1g/cm3，需水量较少，保水性和抗冻性差。由于减少了熟料，水化热变低，而抗硫酸盐腐蚀能力提高。不宜用于冬季施工和要求早期强度较高的工程，适于高湿度环境和长期处于水下的工程。在28天后强度有可能继续增长而超过普通硅酸盐水泥。用矿渣水泥的混凝土易泌水而不易振捣密实，不宜用于有较高抗渗要求的混凝土。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条