1) optical high temperature microscope
高温光学显微镜
2) high-temperature optical microscope
高温光学金相显微镜
1.
For original position investigation of Al-Mg and Al-Cu,binary alloy powders during sintering a high-temperature optical microscope was employed,and the regularities in sintering of pure metal powders whose binary alloys have eutectic were revealed.
采用高温光学金相显微镜对Al-Mg和Al-Cu等纯金属粉末构成的二元合金体系进行烧结的原位观察,发现了具有共晶反应的纯金属粉末的烧结规律,并直接观察到晶界作为快速扩散通道的现象。
3) high temperature optical microscope
光学高温金相显微镜
1.
A high temperature optical microscope was used to in-situ investigate the sintering process of Al-10Mg binary system.
利用光学高温金相显微镜对Al 1 0Mg二元纯金属粉末体系的烧结过程进行原位观察 ,发现在镁颗粒内部晶界优先熔化 ,这是由于铝沿镁晶界的扩散系数远高于晶内扩散系数 ,在镁的晶界优先满足共晶的浓度条件而熔化造成的 ,从而直接证实晶界确是元素扩散的一条快速通道。
4) high temperature microscope
高温显微镜
1.
Observation of oxidation process of diamond with high temperature microscope;
用高温显微镜直接观测金刚石的氧化过程
2.
The hot tensile strain process of the microstructure of duplex stainless steel was investigated with high temperature microscope(CSLM).
本文利用共聚焦激光扫描高温显微镜(CSLM)等设备对双相不锈钢的高温拉伸微观变形过程进行了研究。
3.
Pictures of high temperature microscope show that the sintering process can be divided into four stepps.
高温显微镜图片表明,制品的烧结过程可以分为4个阶段。
5) microscope
[英]['maɪkrəskəʊp] [美]['maɪkrə'skop]
光学显微镜
1.
Sum modified-Laplacian(SML) operator has been proposed as focusing measuration to measure the relative sharpness of image sequence that captured from microscope at different distance to locate the height of surface of wear debris, and reconstruct the 3D image of wear-debris.
在铁谱分析中引入计算机三维测量与重构技术,通过使用改进拉普拉斯算子对在普通光学显微镜下拍摄到的磨粒连续图像序列进行清晰度分析来测量磨粒表面高度,重构磨粒三维图像。
6) optical microscopy
光学显微镜
1.
Near-field optical microscopy, based on scanning sample surfaces by the tip of optical probe, obtained the imagined information about the object surface.
近场光学显微镜是利用探针的扫描来获得样品表面信息的。
2.
In this thesis, by using time-resolved small angle light scattering and optical microscopy, the phase separation of hollow glass beads filled polystyrene and poly (vinyl methyl ether) blends are studied.
本论文以聚苯乙烯(PS)和聚甲基乙烯基醚(PVME)共混物作为聚合物基体，结合实时的小角激光散射方法以及光学显微镜方法，对空心玻璃微珠填充的PS／PVME体系的相分离进行理论研究。
补充资料：光学分析显微镜
光学分析显微镜
曝光学分析显微镜
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条