1) Two Side Immersed Nozzle
两侧孔浸入式水口
2) Two-Side Hole Immersed Nozzle
两孔浸入式水口
3) 3-hole SEN
三孔浸入式水口
1.
Detailed predictions on the fluid flow,heat transfer and solidification in mold were obtained regarding the difference between 3-hole SEN and ge.
4对结晶器内钢水流场和传热凝固进行了数值模拟,主要研究了三孔浸入式水口的冶金特征及其对结晶器内钢水流场和温度场的影响。
4) quadripuntal SEN
四孔浸入式水口
1.
The optimization of flow field of quadripuntal SEN of mould of FTSC thin slab has been studied by applying the commercial program PHOENICS.
利用PHOENICS软件对FTSC薄板坯结晶器四孔浸入式水口形成的结晶器流场、冶金特点进行了优化研究,FTSC薄板坯采用四孔浸人式水口,出口流速小,使紊流和弯月面下速度减至最小。
6) submerged entry nozzle
浸入式水口
1.
Analysis on Clogging of Submerged Entry Nozzle for 409L Stainless Steel Concasting and Improved Measure;
409L不锈钢连铸浸入式水口结瘤分析和改进措施
2.
The effect of opening at the bottom of submerged entry nozzle on molten steel flow and temperature distribution in crystallizer;
浸入式水口底部开孔对结晶器内钢液流动和温度分布的影响
3.
Optimization geometry of submerged entry nozzle for bloom continuous casting mould;
大方坯连铸结晶器浸入式水口结构优化
补充资料：铝碳浸入式水口
铝碳浸入式水口
alumina graphite submerged nozzle
制造中要求原料必须符合工艺要求，配料要准确，泥料要造粒，成型压力为120~150MPa。采用无氧化烧成，烧成温度100。、一1350℃。为了提高铝碳质浸入式水口的使用寿命，可以在渣线部位复合一层错碳层。该制品用于连铸中间罐至结晶器之间的钢水保护浇注。制品要干燥保存，必须预热方能使用。必要时，可以在渣线部位以上，用2一3mm厚的耐火纤维纸或套包住，加以保温，防止在开浇时水口堵塞。 (周川生)IUtanJ一nrush.shuikou铝碳浸人式水口(alumina graphite submer-gednozzle)以刚玉和鳞片状石墨为主要原料烧成的用作浸入式水口的碳结合制品。其特点是对钢种适应性强，特别适宜于浇注含锰较高的钢种，耐钢水和熔渣侵蚀性好，使用寿命长。 铝碳质浸入式水口的理化指标如下:A1203)48%，F.C)30%，体积密度)2.329/c m3，显气孔率成18%，耐压强度异22MPa，抗折强度(1 400℃))gMPa，线膨胀率(一000℃)小于0.5%。其制造工艺是以刚玉和石墨为主要原料功口入少量添加剂，采用酚醛树脂作结合剂，经混练、造粒后，在等静压机上成型。半成品经干燥后，在无氧化烧成窑内烧成。经加工、无损探伤和喷涂防氧化涂料后即为成品。其工艺流程见_图，退份- 成品 铝碳浸入式水口制造工艺流程
说明：补充资料仅用于学习参考，请勿用于其它任何用途。