1) Cr12 Ferrite Heat Resistant Steel
Cr12铁素体耐热钢
2) T91 ferritic heat-resistant steel
T91铁素体耐热钢
1.
The influences of quenching rate in a wide range of 10-6000℃/min on martensite transformation starting temperature,Ms,of T91 ferritic heat-resistant steel were studied by DIL805A/D high-resolution differential dilatometer.
利用Baehr DIL805高精度差分膨胀仪,通过对线膨胀行为的测量与分析,获得相关动力学信息,系统研究了不同淬火速率(10~6000℃/min)对T91铁素体耐热钢马氏体转变开始温度Ms的影响。
2.
The critical cooling rates in undercooled austenite transformation process of T91 ferritic heat-resistant steel were studied by DIL805A/D high-resolution differential dilatometer.
利用DIL805A/D高精度差分膨胀仪,通过线膨胀行为测量与微观组织分析,获得T91铁素体耐热钢连续冷却转变过程中相关动力学信息,结合冷却后T91钢组织特征,确定了T91钢过冷奥氏体转变过程中的临界冷却速度。
3) ferrite refractory steel
铁素体耐热钢
1.
The 409L ferrite refractory steel has been developed successfully.
成功研制了409L铁素体耐热钢,通过对其工艺和性能的分析研究,表明409L铁素体耐热钢具有良好的冷热加工性;良好的焊接性;并在中、低温环境下使用具有良好的抗氧化性能。
2.
The 409L ferrite refractory steel has been prepared successfully.
成功研制了409L 铁素体耐热钢,通过对其工艺和惟能的分析和研究,表明409L 铁素体耐热钢具有良好的冷热加工性,良好的焊接性,并在中、低温环境下使用具有良好的抗氧化性能。
6) T91 ferritic heat resistant steel
T91铁素体耐热钢
1.
The effect of thermomechanical treatment processing(immediate quenching after deformation in the austenite non-recrystallization region)on microstructures of T91 ferritic heat resistant steel was investigated by compressive deformation performed on a Gleeble 1500 thermomechanical simulator.
在 Gleeble 1500热模拟实验机上采用热压缩实验方法,研究了形变热处理工艺即在奥氏体未再结晶区变形后直接淬火对 T91铁素体耐热钢微观组织的影响。
补充资料：铁素体耐热钢
分子式：
CAS号：
性质：含铬17％以上的基体为铁素体组织的一类耐热钢。含铬11％～17％的钢抗氧化性极限温度为800～850℃，在更高温度下容易发生急剧的异常氧化。为提高这一极限温度，开发了高铬并添加少量硅、铝、钇和稀土类元素的耐热钢。这类钢的高温强度不如奥氏体耐热钢，也比马氏体耐热钢的强度低，它们适合于要求抗氧化性比高温强度更重要的部位上。典型的钢种有18Cr钢、19Cr-3A1钢。在18Cr钢中通过添加少量锆、钛和稀土元素等，开发成功一系列抗氧化性显著改善了的铁素体耐热钢。
CAS号：
性质：含铬17％以上的基体为铁素体组织的一类耐热钢。含铬11％～17％的钢抗氧化性极限温度为800～850℃，在更高温度下容易发生急剧的异常氧化。为提高这一极限温度，开发了高铬并添加少量硅、铝、钇和稀土类元素的耐热钢。这类钢的高温强度不如奥氏体耐热钢，也比马氏体耐热钢的强度低，它们适合于要求抗氧化性比高温强度更重要的部位上。典型的钢种有18Cr钢、19Cr-3A1钢。在18Cr钢中通过添加少量锆、钛和稀土元素等，开发成功一系列抗氧化性显著改善了的铁素体耐热钢。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。