1) gold-nickel alloys
金镍合金
2) nickel and nickel alloy
镍及镍合金
1.
The result indicated that it was important for nickel and nickel alloy to control heat temperature and atmosphere in heat stove or heat treatment and protect from sulfur brittleness in making the heads and pressure vessels.
镍及镍合金具有优异的耐腐蚀性能 ,但在高温含硫气体中易腐蚀变脆 ,产生硫脆现象。
3) Zn-Ni alloy
锌镍合金
1.
A glow discharge spectrometer(GDA-750) and a scanning electron microscope(Hitachi S-S70 SEM) were used to investigate the effects of the electroplating processing parameters on the Ni content,thickness,and appearance of the Zn-Ni alloy coating.
通过正交试验方法,采用新的添加剂和配位剂实现了锌镍合金电镀,优选出了新的锌镍合金电沉积工艺和镀液配方。
2.
Ammonium-free weak acidic electroplating technology for Zn-Ni alloy was developed.
研究了一种无铵弱酸性锌镍合金电镀工艺,并深入探讨了镀液的成分及工艺条件对镀层含镍量的影响,得到了镀层为γ相Ni5Zn21与δ相Ni3Zn22、且含镍量为13%的全光亮锌镍合金镀层,确定了电镀工艺规范。
3.
In this article,the effects of rare earth on Zn-Ni alloy electroplating from sulfate bath have been studied.
研究了稀土在硫酸盐体系电镀锌镍合金中的作用。
4) nickel-based alloy
镍基合金
1.
Studies of static recrystallization of new nickel-based alloy;
新型镍基合金静态再结晶规律研究
2.
Analysis of two nickel-based alloys used in absorber of wet flue gas desulphurization in coal-fired power plant
燃煤电厂湿法烟气脱硫吸收塔镍基合金材料国产化可行性分析
5) Zinc-nickel alloy
锌镍合金
1.
Selection of complexing agents for cyanide-free alkaline zinc-nickel alloy electroplating;
无氰碱性锌镍合金电镀中配位剂的选择
2.
Studies on white chromating of zinc-nickel alloy electrodeposited from alkaline bath;
碱性锌镍合金电镀白钝化工艺的研究
3.
Formula of Zinc-nickel alloy electroplatings from high ammonium chloride and weak acidic solutions was presented.
提出了连续电镀锌镍合金的高氯化氨 弱酸型镀液工艺参数 ,对镀液成分、pH值、温度、阴极电流密度对镀层镍含量的影响及连续电镀锌镍合金的镀速控制等问题进行了研究。
6) Ti-Ni alloy
钛镍合金
1.
A new kind of boron nitride based shell mold used for investment casting titanium alloys was fabricated and the reaction between it and Ti-Ni alloy was investigated.
研究了一种新型钛合金精密铸造用型壳——氮化硼基复合型壳及其与钛镍合金的界面反应和反应层的形成机制。
2.
The practicability on Ti-Ni alloy manufactured by direct electrochemical reduction of TiO2 and NiO oxides was investigated.
研究了利用熔盐电解法从金属氧化物中直接电解制备钛镍合金的可行性。
补充资料：金镍合金
分子式：
CAS号：
性质： 金基添加镍的二元合金，在850℃以上为连续固溶体，低温下分解为富金和富镍的两相固溶体。有AuNi5、AuNi9、AuNil0和AuNi18等合金。采用真空感应炉熔炼，合金凝固后水淬。小于10％M的合金可用冷加工成材；大于18％M的合金经软化处理后，再热加工和冷加工成材。广泛用作轻、中负荷电接触材料；AuNil8、AuNi45等用作电真空钎料，钎接航空发动机叶片。
CAS号：
性质： 金基添加镍的二元合金，在850℃以上为连续固溶体，低温下分解为富金和富镍的两相固溶体。有AuNi5、AuNi9、AuNil0和AuNi18等合金。采用真空感应炉熔炼，合金凝固后水淬。小于10％M的合金可用冷加工成材；大于18％M的合金经软化处理后，再热加工和冷加工成材。广泛用作轻、中负荷电接触材料；AuNil8、AuNi45等用作电真空钎料，钎接航空发动机叶片。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条