1) Ni-P alloy
镍磷合金
1.
Preparation of bulk amorphous Ni-P alloy by electrochemical deposition and its structure research;
块状非晶态镍磷合金的电化学沉积制备与结构研究
2.
Anti-corrosion properties of Ni-P alloy deposits preparedfrom electrolytes containing NaH_2PO_2·H_2O;
次磷酸盐体系电镀镍磷合金镀层的耐蚀性能
3.
Electroless Ni-P alloy deposits have been widely adopted in industries for their excellent properties.
由于具有优良的性能,化学镀镍磷合金在工业上得到了广泛应用。
2) nickel-phosphorus alloy
镍磷合金
1.
Research on TL full-bright electroless nickel-phosphorus alloy plating;
TL全光亮化学镀镍磷合金工艺研究
2.
Electroless nickel-phosphorus alloy plating on 45~# carbon steel;
45号钢表面化学镀镍磷合金
3.
Studies on the mechanism of amorphous nickel-phosphorus alloy electrodeposition;
非晶态镍磷合金电沉积机理的研究
3) Ni P alloy
镍磷合金
1.
Compared to electroless nickel phosphorus plating, Ni P alloy electroplating has the advantages such as rapid deposit rate, low bath temperature, high bath stability, thick deposit, and low cost.
对几种电镀镍磷合金镀液进行比较,通过中性盐雾试验,全浸泡腐蚀试验,镀层孔隙率、结合力和硬度测试,得到溶液的主要成分为硫酸镍、氯化镍、次亚磷酸钠、硼酸、氟化钠,并研究了次亚磷酸钠的含量和阴极电流密度对镀层硬度和耐蚀性的影响。
2.
A low phosphorous and low temperature alkaline electroless Ni P alloy plating process applicable to polyurethane sponge substrate is obtained through screening complexing, reducing and other relevant agents.
通过络合剂、还原剂等的筛选 ,确定了一种低磷含量且适合于聚氨酯海绵基体的低温碱性化学镀镍磷合金工艺 ,并研究了镀液的工艺性
3.
Electroless Ni P alloy coating has excellent performances due to its amorphous structure.
化学镀镍磷合金镀层由于其非晶态结构而具有优异的性能。
4) Ni-P coating
镍磷合金
1.
The results show that the anti-corrosion properties of Ni-P coating on Al alloy is better than stainless steel,and conductive performance is better than stainless,and can meet the requirement of the bipolar of .
以铝合金为基体材料,采用碱性-酸性双溶液体系化学镀镍磷合金,研究了镍磷合金镀层的耐蚀性和热处理对耐蚀性的影响,测定了镍磷合金镀层及改性铝合金的导电性能。
6) nickel-phosphorus alloy
镍-磷合金
1.
Current status of research on preparation technologies including technological conditions such as bath components,plating conditions,anode composition etc,and properties of electrodeposited nickel-phosphorus alloy was summarized.
对电沉积镍-磷合金的工艺与性能进行了综述,包括镀液成分、镀覆条件、阳极组成等工艺条件的研究现状,并介绍了合金镀层的物相结构、非晶态与晶态之间的转化和不同成分的镀层的硬度、耐磨性、耐蚀性及影响这些性质的因素。
补充资料：镍磷合金电镀
分子式：
CAS号：
性质：含磷量大于8%以上的镍磷合金有良好的非晶态结构，其耐蚀性、耐磨性甚佳，经适当温度热处理，维氏硬度可达1100左右，此时镀层的耐磨性与硬铬镀层相媲美。此外，还具有良好的焊接性、电学性能和磁性等。因此，广泛用于电子工业、计算机工业、宇航工业领域。镍磷合金镀层可通过电镀或化学镀的方法得到。电镀溶液主要有镍盐-亚磷酸镀液和镍盐-次磷酸镀液。前者要在低PH值下施镀，其阴极电流效率较低。后者可在较高PH值下电镀，但次磷酸根离子在阳极上易被氧化。两种溶液的稳定性都应采取适当措施加以控制。
CAS号：
性质：含磷量大于8%以上的镍磷合金有良好的非晶态结构，其耐蚀性、耐磨性甚佳，经适当温度热处理，维氏硬度可达1100左右，此时镀层的耐磨性与硬铬镀层相媲美。此外，还具有良好的焊接性、电学性能和磁性等。因此，广泛用于电子工业、计算机工业、宇航工业领域。镍磷合金镀层可通过电镀或化学镀的方法得到。电镀溶液主要有镍盐-亚磷酸镀液和镍盐-次磷酸镀液。前者要在低PH值下施镀，其阴极电流效率较低。后者可在较高PH值下电镀，但次磷酸根离子在阳极上易被氧化。两种溶液的稳定性都应采取适当措施加以控制。