1) Ni60 alloy
Ni60合金
1.
The microstructure and phase of vacuum sintered Ni60 alloy were analyzed by SEM, EDS, XRD and Thermo-Calc software.
采用扫描电镜、能谱仪和X射线衍射等方法对Ni60合金真空烧结后的金相组织进行了观察和相的分析,并利用Thermo-Calc软件对Ni60中的组成相进行了研究。
2.
The experimental study of cladding with the Ni60 alloy powder on the surface of 45 steel using the CO_2 laser under the condition of no preheating and post-treatment was studied.
在无预热、后处理等条件下,利用CO2激光器在45钢表面进行了Ni60合金粉末熔覆的试验研究。
3.
Stellie6 alloy powder and Ni60 alloy powder were cladded respectively on the surface of Cr12MoV mould steel using a 5kW CO_2 laser.
利用5kW的横流CO2激光器在Cr12MoV钢表面分别熔覆Stellie6和Ni60合金粉末,并利用X射线衍射、光学显微镜分析了合金熔覆层的金相组织和相组成;测量了合金熔覆层的显微硬度,并用M-200环-块磨损试验机研究了其磨损性能。
2) Ni60 self-fluxing alloy
Ni60自熔合金
3) Ni-60 alloy cladded layer
Ni60合金熔覆层
4) self-fusing alloy powder Ni60
Ni60自熔性合金粉末
5) Ni60/WC composite coating
Ni60/WC复合涂层
1.
Investigation of microstructure and properties of AC-HVAF sprayed Ni60/WC composite coating;
AC-HVAF喷涂Ni60/WC复合涂层组织及性能研究
2.
Ni60/WC composite coating is prepared using advanced AC-HVAF spray on 0Cr13Ni5Mo stainless steel.
利用先进的AC-HAVF喷涂技术在0Cr13Ni5Mo不锈钢上制备了Ni60/WC复合涂层。
6) Ni 60 spray welded coating
Ni60喷焊层
补充资料：Ni3Al基金属间化合物高温合金
Ni3Al基金属间化合物高温合金
Ni_(3)Al-base intermetallic compound superalloy
N一3AIJ一J旧shuJ一an huahewu goowen heJ一nNi3AI基金属间化合物高温合金(Ni3AI一baseintermetallie eompound superalloy)以Ni3AI相为基体的金属间化合物高温合金。Ni3AI作为高温合金材料中的强化相口)早已被人们所熟知。单晶Ni3AI有较好的室温塑性和加工性，但多晶Ni3AI在室温的塑性儿乎为零。1979年，日本和泉修等发现，添加微量硼可使Ni3AI韧化。硼强烈地偏聚于晶界，从而提高晶界的结合强度并使晶界区无序化，因此提高了晶界区塑性变形能力，使Ni3AI的室温拉伸伸长率可达50%以上。纯净N珠AI的室温、高温强度偏低，与高温合金相比需要进一步提高。固溶强化(见高温合金固溶强化)是提高强度的一条有效途径。Ni3AI可以固溶很多元素，其中以错和铅的强化效果最显著。美国橡树岭国家试验室已发展了一系列含铬、错、错等元素的Ni3AI基金属间化合物高温合金，具有良好的强度、塑性和高温抗氧化性。中国也对Ni3AI基合金进行了深入研究，并添加微量镁显著改善了热加工塑性。Ni3AI基合金可能是最先在工业上得到使用的金属间化合物高温合金之一，已制成各种部件在试用，如汽轮机和柴油机的耐热部件、高温模具、加热元件以及航空用的紧固件等。 〔邹敦叙)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条