1) self-setting
自固化
1.
Porous hydroxyapatite/β-calcium phosphate ceramic scaffolds with macropore sizes of 200-400μm and micropore sizes of about 1μm were prepared by coating porous polyurethane template with αcalcium phosphate bone cement (CPC) slurry, and its subsequent hydrolysis to calcium deficient hydroxyapatite (HA) during the self-setting processes is presented.
以聚氨酯泡沫为多孔模板,α磷酸钙骨水泥为浆料体系,将浸渍法和骨水泥自固化特性相结合,制备大孔尺寸为200~400μm、贯穿式微孔尺寸约为1μm的多孔磷酸钙复相陶瓷支架。
2.
In order to improve the bioactivity of porous polymer scaffold, porous biocomposite was prepared by modifying porous polyurethane template using a coating method according to the “self-setting” characteristic of α-tricalcium phosphate (α-TCP) bone cement in a moist environment.
为了改善有机多孔支架的生物活性,利用磷酸钙骨水泥在潮湿空气中的自固化特性,以α-磷酸钙骨水泥为浆料体系,采用涂覆法对多孔聚氨酯进行表面修饰,获得了表面被羟基磷灰石(Ca10(PO4)6(OH)2,HAp)修饰层包裹的多孔复合材料。
3.
Calcium phosphate cement (CPC) is a new type of self-setting materials for bone repairing,which has attracted attention of scientists in the world because of its excellent biocompatibility,osteoconductivity,biodegradability and remodellable properties and consequently has a promising prospect in extensive applications.
磷酸钙骨水泥(CPC)作为一种新型的自固化型骨修复材料,因其具有良好的生物相容性、骨传导性、可降解性及可塑性等优点,受到了国内外众多学者的广泛关注,具有广阔的应用前景。
2) radical curing
自由基固化
3) settting time
自固化时间
4) self-immobi lization
自已固定化
6) self-emulsifiable curing agent
自乳化固化剂
补充资料：自固化胶黏剂
分子式：
CAS号：
性质：通常是由于吸收了空气中的水分，使混有固化剂的胶黏剂在室温下发生交联反应而固化。如氰基丙烯酸酯胶黏剂。