1) in-situ crystallization
原位晶化
1.
The pore structure and the process of in-situ crystallization of zeolite Y prepared from kaolin are investigated by N_2 static adsorption and IR spectrum method.
采用N2静态吸附法和IR光谱法研究了高岭土原位晶化合成Y型沸石过程中的孔结构和沸石的形成过程。
2.
Properties of Shanxi Jinyang kaolin and FCC catalyst prepared via its in-situ crystallization were studied.
结果表明,山西金洋土在原位晶化体系中具有适度活性硅和较快活性铝的碱溶速率,有良好的晶化性能和裂化性能。
3.
Kaolin in-situ crystallization catalyst prepared via an in-situ crystallization method was modified by vanadium.
具体工作如下:应用原位晶化技术合成了高岭土型催化剂,选择金属元素钒作为功能组分对高岭土型催化剂进行改性,然后对改性前后的高岭土型催化剂进行X-射线衍射和比表面分析。
2) in situ crystallization
原位晶化
1.
The properties of Hancheng kaoline and the FCC catalyst from its in situ crystallization were studied in the laboratory.
在实验室进行了韩城高岭土的性质及其原位晶化所制FCC催化剂的研究。
3) in-situ synthesis
原位晶化
1.
The method for in-situ synthesis of ZSM-5 has significant advantages compared to the additive’s traditional preparation.
基于此,本论文旨在开发新型多产丙烯ZSM-5分子筛催化材料,即在高岭土微球或固体硅胶小球上原位晶化合成ZSM-5分子筛,使反应物分子直接接触活性组分进行反应,进而提高ZSM-5分子筛活性组分的利用率。
4) direct in situ crystallization
直接原位晶化
5) Aging/in-situ polymerization
晶化/原位聚合
补充资料：多晶莫来石晶须(纤维)
分子式：
CAS号：
性质：莫来石相为主晶相的多晶纤维。化学成分为Al2O3 72％～77％，SiO222％～17％，B2O3 3％～5％，P2O51.5％～3.0％。纤维直径2～7μm，纤维长度20～125μm。使用温度1350℃。多采用溶胶-凝胶法制造。主要用作补强填料，也可作为轻质、隔热保温材料使用。
CAS号：
性质：莫来石相为主晶相的多晶纤维。化学成分为Al2O3 72％～77％，SiO222％～17％，B2O3 3％～5％，P2O51.5％～3.0％。纤维直径2～7μm，纤维长度20～125μm。使用温度1350℃。多采用溶胶-凝胶法制造。主要用作补强填料，也可作为轻质、隔热保温材料使用。