1) water-quenched slag
水淬渣
1.
The experimental results showed that under the conditions with the ratio of the water-quenched slag and rectorite of 1∶1,the amount of the additive(IS) of 10%,the amount of 50% water,and the roasting temperature of 400 ℃,the spallation loss ratio of granulated composite material prepared was 0.
结果表明:水淬渣与累托石的比例为1∶1,另加入10%的添加剂(IS)和50%的水,焙烧温度为400℃,制成的复合颗粒材料的散失率为0。
2.
Factors affecting flotation of water-quenched slag from a copper smelting plant in Hubei province,such as grinding fineness,pulp density,pH value and the reagent system,were studied.
对湖北某铜冶炼厂的炼铜水淬渣(含铜1。
3.
The optimum conditions for flotation of the water-quenched slag are as follows: natural pH,Na2S 800 g/t,mixed collecting agent 240 g/t,flotation time 6 min,percent of 74 μm particles 95% and solid content 30%.
在铜熔炼反射炉渣中铜铁赋存状态分析基础上,采用常规选矿和火法贫化工艺对反射炉水淬渣进行回收铜技术探索。
2) water quenched slag
水淬渣
1.
Process of desilication under high temperature-magnetic separation was adopted for iron recovery from water quenched slag of copper smelting.
采用高温脱硅—磁选工艺从炼铜水淬渣中回收铁。
3) melting slag water quenching
熔渣水淬
4) slag quenching
钢渣水淬
1.
The measures of steel-making with less-slag, BOF gas recycle, slag quenching and slab hot charge are carried out in the No.
济钢第一炼钢厂通过采取少渣炼钢、煤气回收、钢渣水淬、铸坯热送等措施,达到了充分回收和利用能源、合理使用资源、降低系统能耗、减少污染物排放、实现节能、清洁生产的目的,吨钢钢铁料消耗、炼钢工序能耗、耐材消耗分别降至1082kg、1045524。
5) water quenching slag
水淬矿渣
1.
Research on super-fine powder in water quenching slag for cement production;
水淬矿渣微细粉配制水泥的研究
6) Water Hardening Coal Dust
水淬煤渣