1) copper-coated TiB2
镀铜二硼化钛
1.
Three types of brushes are made from the composites of TiB2-Cu-C,copper-coated TiB2-Cu-C and Cu-C by means of powder metallurgy.
对比3种复合材料电刷的磨损量,发现加二硼化钛的最高,铜-石墨的次之,加镀铜二硼化钛的最低。
2) TiB2
二硼化钛
1.
In theory the discharge capability of BaFeO4 cathode is 313 mA ·h/g due to its three-electron reaction and that of TiB2 anode is 2 314 mA ·h/g due to its six-electron reaction.
以高铁酸钡为正极材料,二硼化钛为负极材料,碱性氢氧化钾溶液为电解质构成了一次性碱性电池。
2.
The relations between composition,electronic structure,chemical bond and property of composites of Ti-Al-C/TiB2 and related single phases are researched using density function theory and discrete variation,the first principle method(DFT-DVM).
用离散变分密度泛函第一原理计算方法研究了三元层状碳化物/二硼化钛复合陶瓷及相关单相系列材料,讨论了材料组成、电子结构、化学键与性能等之间的变化规律。
3) titanium diboride
二硼化钛
1.
Study on Acid Washing Process of Producing Titanium Diboride by SHS Technology;
自蔓延法生产二硼化钛的酸洗过程研究
2.
Porous TiB2 ceramics with high strength and high porosity has been successfully fabricated using titanium diboride as raw materials by the spark plasma sintering technique.
以二硼化钛微粉为原料,采用放电等离子烧结技术,通过控制烧结温度、保温时间、施加压力等工艺参数,成功的制备出具有高强度和高气孔率的二硼化钛多孔陶瓷。
3.
The carbothermic method of preparation for titanium diboride with titanium oxide and boron oxide in an arc furnace is studied.
研究了电弧炉碳热还原氧化钛和氧化硼制取二硼化钛的方法，制备出相对纯度大于９５％的二硼化钛。
4) titanium diboride/iron
二硼化钛/铁
5) titanium diboride-alumina
二硼化钛-氧化铝
6) titanium diboride/nickel aluminides
二硼化钛/铝化镍
补充资料：镀铜
镀铜
copper coating
dUtong镀铜(eopper eoating)在酸洗后的盘条(线坯)表面镀覆一层铜，以作为拉丝时的润滑载体。以铜层作润滑载体主要用在拉拔轮胎钢丝与气体保护焊丝等特殊场合，这时铜层除用作润滑载体外，可提高轮胎钢丝同橡胶的结合力和焊丝的导电性。此外也用于弹妥钢丝等的生产中，以改善拉拔时的润滑性能及产品的表面质量。 镀铜操作时，把盘条浸入加有一定硫酸和骨胶的硫酸铜溶液中。根据电位序，铁能置换铜: Fe+CuZ+-今Cu+FeZ+并很快发生下列反应和完成镀铜过程 Fe+CuSO;一FeSO‘+Cu专硫酸铜是溶液的主要镀剂，提供铜离子的来源，浓度通常控制在60一7馆/L。浓度过低，将延长镀铜时间且不易获得所需厚度的镀层;浓度过高，则铜的沉积速度过快，导致铜结晶迅速长大，使镀层疏松、粗糙，影响与基体的结合。硫酸的主要作用是活化盘条表面，使铜层能与基体牢固结合。骨胶有促使铜与基体粘合的作用，并使铜层结晶细密。镀铜时溶液温度必须控制在簇25℃，温度较低时，镀层光亮致密，但生产率低。温度过高时，则镀层厚，且粗糙、疏松、附着力差。溶液中Fe2+离子过多会恶化镀层质量。镀铜过程约在1一2而n内完成。 (韩观昌)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。