1) Methyl hydrogen silicone fluid
甲基含氢硅油
1.
The influence of titanium isopropoxide on the anti-contamination agent curing speed in benzinum solvent , and the influence of methyl hydrogen silicone fluid and titanium isopropoxide content on the proofing functio.
文中还讨论了以石油醚为溶剂的钛酸四异丙酯对防污剂固化速度的影响以及甲基含氢硅油和钛酸四异丙酯的含量对防污性的影响。
2.
This paper also studied the proofing function influence produced by methyl hydrogen silicone fluid content and tita.
讨论了以石油醚为溶剂钛酸四异丙酯对防污剂固化速度的影响、甲基含氢硅油和钛酸四异丙酯的含量对防污性的影响。
2) methylphenyl hydro-silicone fluid
甲基苯基含氢硅油
1.
Here we reported a kind of methylphenyl hydro-silicone fluid which serves as liquid crosslinking agent for LED encapsulant.
产物为澄清透明的甲基苯基含氢硅油,其苯基含量(Ph/Si,molar ratio)为0。
3) ethylhydrosilicone fluid
乙基含氢硅油
4) poly(methylhydrosiloxane)
含氢硅油
1.
Synthesis and characterization of poly(methylhydrosiloxane)with n-butyl methacrylate;
甲基丙烯酸正丁酯-含氢硅油的合成与表征
2.
01%) of the raw material weight,a series of water-based fluorosilicone were synthesized by using poly(methylhydrosiloxane),organoflurine,allyl polyoxyethylene polyoxypropylene ether,and silicane coupling agent.
01%以及无溶剂的条件下,采用硅氢加成法将烯丙基聚氧乙烯聚氧丙烯醚、含氟单体及硅烷偶联剂与低含氢硅油进行接枝共聚,成功地制备了一系列有机氟硅聚合物。
3.
Without solvent, a series of water-based fluorosilicone polymers were synthesized from allyl polyoxyethylene polyoxypropylene ether, organic fluoride and poly(methylhydrosiloxane) via hydrosilyla- tion, and the aqueous dispersions of the polymers were obtained by the way of emulsification.
在无溶剂的条件下,通过硅氢加成法将烯丙基聚氧乙烯聚氧丙烯醚,氟化丙烯酸烷基酯接枝共聚到甲基含氢硅油侧链,成功地合成了一系列有机氟硅聚合物。
5) hydrogen containing silicone fluid
含氢硅油
1.
Polyether modified polysiloxane was synthesized by the hydrosilation reaction of hydrogen containing silicone fluid (PHDS)and allyl polyether(APE), using chloroplatinic acid as the catalyst.
以氯铂酸为催化剂 ,利用含氢硅油 (PHDS)与烯丙基聚醚 (APE)的硅氢加成反应 ,合成出聚醚改性硅油 ;然后用乙醇胺进行胺化反应 ,制成纸张用氨基改性聚醚硅油柔软剂。
2.
s:Mass fraction of active hydrogen in hydrogen containing silicone fluid was calculated bases on integrate area of testable hydrogen proton peak by 1 H NMR taking benzene as classic inner standard matter.
以苯为内标物 ,采用核磁共振 ( 1HNMR)法 ,根据可测试的氢质子峰的积分面积 ,计算出含氢硅油中活性氢的质量分数。
6) h-silicone oil
含氢硅油
1.
The wool fabric was treated by amino silicone oil,h-silicone oil combine with low temperature plasma(LTP) to improve the anti-felting property.
经氨基硅油处理后等离子体照射,再用含氢硅油处理后等离子体照射工艺处理的羊毛织物,毡缩率降低到7。
2.
The wool fabric was treated by amino silicone oil,h-silicone oil combine with low temperature plasma(LTP)to improve the anti-felting property.
经氨基硅油处理后等离子照射,再用含氢硅油处理后等离子照射工艺处理的羊毛织物毡缩率降低到7。
补充资料：甲基含氢硅油
分子式：
CAS号：
性质：无色透明油状物，黏度一般为(1～5)×10-2Pa·s，相对密度0.98～1.10，折射率1.390～1.410，氢含量0.8％～1.4％。在醇碱作用下，Si-H键断裂，放出氢气。在铂催化剂作用下，S-H键可与链烯烃进行加成反应。当温度大于50℃时，可与含环氧基的化合物反应，具有良好的成膜性能。可由甲基二氯硅烷和三甲基氯硅烷共水解缩合来制取。用作防水处理剂，也可用作橡胶和塑料工业的脱模剂、纸张和包装材料的防粘剂。
CAS号：
性质：无色透明油状物，黏度一般为(1～5)×10-2Pa·s，相对密度0.98～1.10，折射率1.390～1.410，氢含量0.8％～1.4％。在醇碱作用下，Si-H键断裂，放出氢气。在铂催化剂作用下，S-H键可与链烯烃进行加成反应。当温度大于50℃时，可与含环氧基的化合物反应，具有良好的成膜性能。可由甲基二氯硅烷和三甲基氯硅烷共水解缩合来制取。用作防水处理剂，也可用作橡胶和塑料工业的脱模剂、纸张和包装材料的防粘剂。