1) methyl silicone oil
甲基硅油
1.
This paper introduces a modification in the technique for purging the methyl silicone oil on the metal circuit board in radar cabinet.
采用四氯化碳为有机溶剂代替酒精,清洗掉了雷达机柜内金属线路板表面铬金属膜上的甲基硅油保护液,使三防漆能够均匀地涂敷在金属线路板表面,可以充分发挥三防漆对雷达机柜内电子装备的防护作用。
2) Silicone oil
甲基硅油
1.
Then these TiO2 particles with high temperature were cooled by putting them to air and silicone oil respectively.
以热分解方法制备纳米TiO_2,后续处理采用甲基硅油淬火改性和自然冷却方法,对改性前后的产物进行了XRD,TEM,FTIR等表征。
3) methyl silicon oil
甲基硅油
1.
The dye fluorescein doped silica/methyl silicon oil (MOS) coating was prepared by the sol-gel method.
采用溶胶-凝胶(Sol-Gel)法制备了掺杂荧光素(FL)的SiO2/甲基硅油(MSO)复合薄膜,并且测定了这种薄膜的光谱特性。
4) simethicone
二甲基硅油
1.
The emulsion of polysiloxane defoaming agent was prepared by diffusion emulsification of simethicone, composite emulsifier and additive in the water phase.
用二甲基硅油、复合乳化剂和助剂在水相中分散乳化,制备出乳液型有机硅消泡剂,并讨论了乳化温度、二氧化硅型号以及乳化剂用量等因素对乳液稳定性和消泡效果的影响。
2.
The emulsion defoamer agent was preparation by using simethicone,H-containing polysilicone,polyether and suitable emulsifying agent.
以二甲基硅油、含氢硅油、聚醚为原料,选用适宜的乳化剂,制成了兼有有机硅特性和聚醚特性的乳液型消泡剂,性能良好,成本低廉,并对硅油聚醚的配比、乳化剂的选择等对消泡效果有影响的因素进行了探讨。
5) dimethyl silicon oil
二甲基硅油
1.
Improvement of anti-foaming characteristic of lubricating oil in waterpump by adding dimethyl silicon oil;
二甲基硅油在改善电泵润滑油抗泡沫性中的应用
2.
A study on preparation and performance of defoamer of bisamide compounded with dimethyl silicon oil/gas phase SiO_2;
乳液型二甲基硅油/气相SiO_2/双酰胺复配消泡剂的制备及其性能研究
3.
The paper elaborated the principle of organ silicon defoamer and the properties of dimethyl silicon oil which was used as the main materials of organ silicon defoamer.
本文阐述了有机硅消泡剂的消泡原理以及用作消泡剂主体材料的二甲基硅油的特性。
6) polydimethylsiloxane
二甲基硅油
1.
Synthesis of polydimethylsiloxane with solid super base Na-KOH/r-Al_2O_3 as catalyst;
固体超强碱Na-KOH_3/r-Al_2O_3催化合成二甲基硅油
2.
This paper recommend a method for preparing 10 - 20 cs polydimethylsiloxane with acid lower-boiling substance.
本文介绍了一种以酸法低沸为主要原料,制备10～20厘沲二甲基硅油的方法。
3.
The frequency and time domain dielectric spectra of polydimethylsiloxane of polymerization degree 50 to 824 are measured in low temperature.
测量了聚合度由５０～８２４的二甲基硅油的频域和时域低温介电谱，其结果和聚合度几乎无关。
补充资料：甲基硅油
分子式：
CAS号：
性质：又称甲基硅油。分子主链由硅氧原子组成，与硅相连的侧基为甲基。25℃下的黏度范围为10～200 000mm2/s。相对密度d4200.93～0.975。折射率nD201.390～1.410。无色透明、无毒无嗅的油状物。具有优异的电绝缘性能和耐热性，闪点高、凝固点低，可在-50～+200℃温度范围内长期使用。黏温系数小，压缩率大，表面张力小，憎水防潮性好，比热容和导热系数小。可由二甲基环硅氧烷在催化剂存在下与六甲基二硅氧烷进行调聚反应来制取。在塑料、橡胶工业中用作脱模剂；在生化、制药、食品工业中用作消泡剂；在机械、仪表工业中用作防震阻尼材料等。
CAS号：
性质：又称甲基硅油。分子主链由硅氧原子组成，与硅相连的侧基为甲基。25℃下的黏度范围为10～200 000mm2/s。相对密度d4200.93～0.975。折射率nD201.390～1.410。无色透明、无毒无嗅的油状物。具有优异的电绝缘性能和耐热性，闪点高、凝固点低，可在-50～+200℃温度范围内长期使用。黏温系数小，压缩率大，表面张力小，憎水防潮性好，比热容和导热系数小。可由二甲基环硅氧烷在催化剂存在下与六甲基二硅氧烷进行调聚反应来制取。在塑料、橡胶工业中用作脱模剂；在生化、制药、食品工业中用作消泡剂；在机械、仪表工业中用作防震阻尼材料等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。