bcc Fe,bcc Fe,在线英语词典,英文翻译,专业英语

1) bcc Fe

bcc Fe

2) bcc Fe

bccFe

3) bcc-Fe

bcc-Fe

SIMULATIONS AND ANALYSIS OF PHASE TRANSFORMATIONS IN bcc-Fe UNDER ISOTHERMAL COMPRESSION;

bcc-Fe等温压缩下相变的微观模拟与分析

4) BCC

BCC

Temperature dependence of atomic states and physical properties of fcc and metastable hcp and bcc Au metals;

fcc,hcp和bcc结构Au的原子状态及物理性质随温度的变化关系

Control software design for BCC;

BCC工艺控制软件设计

BaO-Nd2O3-TiO2(BNT) ceramics were prepared with different additives of BCC(BaCuO2+CuO2) by sol-gel method and solid phase sintering method.

分别以sol-gel法和固相合成法引入BCC(BaCuO2+CuO2)烧结助剂制备BaO-Nd2O3-TiO2(BNT)陶瓷采用DTA-TGA、SEM、网络分析仪等对陶瓷微观结构、性能等进行分析。

5) BCC

BaCuO_2CuO（BCC）

6) BCC

双耳线索编码

Binaural cue coding(BCC) can overcome these problems.

与传统立体声编码相比较,强度立体声编码可以有效地降低码率,但是强度立体声编码的局限性在于,如果对整个带宽或者听觉声像较宽信号进行编码时,会产生令人难以接受的失真,双耳线索编码(Binaual Cue Coding)克服了强度立体声编码的这一问题。

参考词条

bcc structure bcc metals bcc structure BCC check BCC lattice bcc crystal BCC algebra bcc Ni BCC phase BCC_CSM metastable bcc structure bcc hydrogen storage alloy bcc transition metal HCP/BCC interphase boundary biomass compound coal(BCC) FCC/BCC interface structure Ti-containing bcc phase 氧化铝-铬金属陶瓷

补充资料：Fe-C-O和Fe-H-O系平衡图

　　铁及其氧化物与CO-CO₂或 H₂-H₂O 混合气体达到平衡时的气相组成与温度的关系图（图1）。它是由实验测得的数据绘制的，是冶金过程物理化学常用的一种优势区图。图中三条线分别代表下列三个反应的平衡气相组成：
　　570℃以下：Fe₃O₄+4CO3Fe+4CO₂ (1)

　　570℃以上：Fe₃O₄+CO3FeO+CO₂ (2)

　　FeO+COFe+CO₂ (3)

　　3Fe₂O₃+CO─→2Fe₃O₄+CO₂反应达平衡时的一氧化碳分压值太小,几乎与横坐标重合,图中未标出。如果实际气相组成p_co/(p_co+p_co2)高于平衡组成,则反应将向右进行,此时反应式等号右边的固相是稳定的,左边的固相不稳定。图中每条线上方的区域就是该反应式右边固体的稳定存在区。这三条线将整个图划分为三个区域，即Fe、FeO、Fe₃O₄的稳定存在区。三条线交点是四相（Fe、FeO、Fe₃O₄及气相）共存点（见相图）。
　　
　　
　　在钢铁冶炼过程中，常利用此图来确定在给定温度和气相组成条件下能够稳定存在的固相。此图还明确表明铁的各级氧化物是逐级转化的（见Fe-O 状态图）。
　　
　　由图1可见,在虚线(Fe-H-O平衡)与实线(Fe-C-O平衡)交点温度(820℃)以上,H₂比CO具有更强的还原能力；在820℃以下,则正相反。
　　
　　CO对铁还有渗碳作用。当气体中的比值p_co/(p_co+p_CO2)超过反应(4)的平衡组成时，会发生铁的渗碳反应：
　　2CO_(气)─→CO₂(气)+[C] (4)
[C]表示溶解于铁中的碳。图2绘出了一系列 [C]含量下渗碳反应达到平衡时的气相组成与温度的关系曲线。此图直接示出在给定温度和[C]含量的情况下,气相对铁是渗碳还是脱碳。这类问题在钢的热处理时经常遇到。FeO是非化学计量化合物(见Fe-O 状态图)，其中氧含量与其平衡气相组成的关系也在图2中绘出。
　　

说明：补充资料仅用于学习参考，请勿用于其它任何用途。

首页 \| 翻译 \| 影视 \| 论坛 \| 索引 bcc metal bcc crystal BCC model

1) bcc Fe bcc Fe 2) bcc Fe bccFe 3) bcc-Fe bcc-Fe 1. SIMULATIONS AND ANALYSIS OF PHASE TRANSFORMATIONS IN bcc-Fe UNDER ISOTHERMAL COMPRESSION; bcc-Fe等温压缩下相变的微观模拟与分析 4) BCC BCC 1. Temperature dependence of atomic states and physical properties of fcc and metastable hcp and bcc Au metals; fcc,hcp和bcc结构Au的原子状态及物理性质随温度的变化关系 2. Control software design for BCC; BCC工艺控制软件设计 3. BaO-Nd2O3-TiO2(BNT) ceramics were prepared with different additives of BCC(BaCuO2+CuO2) by sol-gel method and solid phase sintering method. 分别以sol-gel法和固相合成法引入BCC(BaCuO2+CuO2)烧结助剂制备BaO-Nd2O3-TiO2(BNT)陶瓷采用DTA-TGA、SEM、网络分析仪等对陶瓷微观结构、性能等进行分析。 5) BCC BaCuO_2CuO（BCC） 6) BCC 双耳线索编码 1. Binaural cue coding(BCC) can overcome these problems. 与传统立体声编码相比较,强度立体声编码可以有效地降低码率,但是强度立体声编码的局限性在于,如果对整个带宽或者听觉声像较宽信号进行编码时,会产生令人难以接受的失真,双耳线索编码(Binaual Cue Coding)克服了强度立体声编码的这一问题。参考词条 bcc structure bcc metals bcc structure BCC check BCC lattice bcc crystal BCC algebra bcc Ni BCC phase BCC_CSM metastable bcc structure bcc hydrogen storage alloy bcc transition metal HCP/BCC interphase boundary biomass compound coal(BCC) FCC/BCC interface structure Ti-containing bcc phase 氧化铝-铬金属陶瓷补充资料：Fe-C-O和Fe-H-O系平衡图　　铁及其氧化物与CO-CO₂或 H₂-H₂O 混合气体达到平衡时的气相组成与温度的关系图（图1）。它是由实验测得的数据绘制的，是冶金过程物理化学常用的一种优势区图。图中三条线分别代表下列三个反应的平衡气相组成：　　570℃以下：Fe₃O₄+4CO3Fe+4CO₂ (1) 　　570℃以上：Fe₃O₄+CO3FeO+CO₂ (2) 　　FeO+COFe+CO₂ (3) 　　3Fe₂O₃+CO─→2Fe₃O₄+CO₂反应达平衡时的一氧化碳分压值太小,几乎与横坐标重合,图中未标出。如果实际气相组成p_co/(p_co+p_co2)高于平衡组成,则反应将向右进行,此时反应式等号右边的固相是稳定的,左边的固相不稳定。图中每条线上方的区域就是该反应式右边固体的稳定存在区。这三条线将整个图划分为三个区域，即Fe、FeO、Fe₃O₄的稳定存在区。三条线交点是四相（Fe、FeO、Fe₃O₄及气相）共存点（见相图）。　　　　　　在钢铁冶炼过程中，常利用此图来确定在给定温度和气相组成条件下能够稳定存在的固相。此图还明确表明铁的各级氧化物是逐级转化的（见Fe-O 状态图）。　　　　由图1可见,在虚线(Fe-H-O平衡)与实线(Fe-C-O平衡)交点温度(820℃)以上,H₂比CO具有更强的还原能力；在820℃以下,则正相反。　　　　CO对铁还有渗碳作用。当气体中的比值p_co/(p_co+p_CO2)超过反应(4)的平衡组成时，会发生铁的渗碳反应：　　2CO_(气)─→CO₂(气)+[C] (4) [C]表示溶解于铁中的碳。图2绘出了一系列 [C]含量下渗碳反应达到平衡时的气相组成与温度的关系曲线。此图直接示出在给定温度和[C]含量的情况下,气相对铁是渗碳还是脱碳。这类问题在钢的热处理时经常遇到。FeO是非化学计量化合物(见Fe-O 状态图)，其中氧含量与其平衡气相组成的关系也在图2中绘出。　　说明：补充资料仅用于学习参考，请勿用于其它任何用途。