1) oxide dispersion strengthened alloy
氧化物弥散强化合金
2) ODS
氧化物弥散强化
1.
Manufacturing Process and Structure Control of ODS MGH 956 Alloy Sheet;
氧化物弥散强化MGH956合金薄板的加工工艺和组织控制
2.
In rencent years,some mechanically alloyed(MA),oxide dispersion strengthened(ODS)ferritc alloy have exhibited dramatically improved high temperature creep properties at high temperatures.
近年来,多种氧化物弥散强化(ODS)铁基高温合金表现出优良的高温力学性能尤其是高温蠕变性能,并且可以比传统铁基高温合金应用于更高的温度。
3) oxide dispersion strengthening
氧化物弥散强化
1.
The in-depth analysis of the mechanism of oxide dispersion strengthening can provide a reference for developing better quality dispersion-strengthened platinum or platinum-rhodium alloys.
运用位错理论,综述氧化物弥散强化Pt/Pt-Rh合金的机理。
4) oxide dispersion strengthened superalloy
氧化物弥散增强高温合金
5) dispersion strengthened copper alloy
弥散强化铜合金
1.
Low content alumina dispersion strengthened copper alloy wa s prepared by short-flow technology, and its annealing characteristics was stud ied by mechanical property measurment, microstructure observation and SEM fractu re analysis.
采用短流程工艺制备了低浓度Cu Al2 O3弥散强化铜合金 ,通过力学性能测量、金相、扫描电镜断口研究了该合金的退火特性。
2.
Fabrications processes and characters of high-strength,high-conductivity and high-heat resistance dispersion strengthened copper alloy are summarized.
综述了高强高导高耐热弥散强化铜合金的制备方法及其特点,比较了各种方法制备的弥散强化铜合金的性能,简述了国内外研究现状。
补充资料：弥散强化MQPt-5Rh合金
分子式：
CAS号：
性质：是以PtRh5合金为基用微细的二氧化锆为强化相的高温结构材料。密度20.6g/cm3。抗拉强度为293MPa。维氏硬度9.2MPa。伸长率22%。电阻系数16.87×10-2Ω·mm2/m。1300℃，5MPa应力下的持久断裂寿命313h，是PtRh10合金的4.47倍。先制成含0.1%Zr的片材，内氧化和复合加工可制成片材、丝材。加工性能良好。用于制作玻璃纤维多孔密排大型（800孔）漏板底板。
CAS号：
性质：是以PtRh5合金为基用微细的二氧化锆为强化相的高温结构材料。密度20.6g/cm3。抗拉强度为293MPa。维氏硬度9.2MPa。伸长率22%。电阻系数16.87×10-2Ω·mm2/m。1300℃，5MPa应力下的持久断裂寿命313h，是PtRh10合金的4.47倍。先制成含0.1%Zr的片材，内氧化和复合加工可制成片材、丝材。加工性能良好。用于制作玻璃纤维多孔密排大型（800孔）漏板底板。