1) mechanical alloying
机械合金化法
1.
W-15Cu composite powders prepared by mechanical alloying of raw powders were consolidated by hot-pressing sintering process,and the influences of sintering process on the properties of W-15Cu alloy were investigated.
以用机械合金化法制备的超细W-15Cu复合粉末为原料,采用热压烧结工艺制备了高密度的W-15Cu合金,用扫描电镜、硬度仪、密度测试仪等研究了烧结工艺对合金组织和性能的影响。
2.
The relevant techniques such as self-propagating high-temperature synthesis,mechanical alloying,microwave method and low temperature chemical method,characteristics and existing problems in preparation are summarized.
对国内外超细TiC粉末的制备技术进行了综述,主要介绍了自蔓延高温合成法、机械合金化法、微波法和低温化学法等的特点及其存在问题,并指出了超细TiC粉末制备技术的发展方向。
2) mechanical alloying
机械合金法
3) MA
机械合金化
1.
Study of the Formation Regularity of the Multi-Component Amorphous Alloys by MA;
机械合金化多元非晶态合金形成规律研究
2.
STUDY OF MACHINE ALLOYING FOR W/Cu MICROPOWDER;
W/Cu二元粉末的机械合金化研究
3.
The Microstructure of Al-10vol%Pb Prepared by MA;
机械合金化制备Al-10vol%Pb组织结构
4) mechanically alloying
机械合金化
1.
Amorphous MgNi hydrogen storage alloy was synthesized by mechanically alloying (MA).
采用机械合金化法制备了MgNi非晶,并对不同制备工艺下的MgNi储氢合金的电化学性能进行了测试。
2.
The Al-Pb-Cu alloy was prepared by mechanically alloying.
用机械合金化方法制备了Al-Pb-Cu合金。
3.
This paper states the mechanism of mechanically alloying & its application in rare earth permanent magnet materials.
简述了机械合金化的机理及其在稀土永磁材料中的应用。
5) mechanical alloying(MA)
机械合金化
1.
In order to improve the condition of synthesizing Ti3SiC2(reducing the sintering centigrade and time, and obtaining Ti3SiC2 of higher purity), a method of mechanical alloying(MA) is adopted to treat the original powder and contrast with element powders (directly mixed DM).
为改善Ti3SiC2的合成条件,利用机械合金化的方法处理原料粉末,并与通常采用的原始粉末直接混合粉末进行比较分析。
2.
7) n-type filled Skutterudite was prepared by mechanical alloying(MA) and subsequent hot pressing(HP).
起始原料使用La、Co、Ni和Sb元素粉末,采用机械合金化(MA)和热压烧结(HP)的方法制备了名义成分为LaxNi0。
3.
Mechanical alloying(MA) is a powerful method in the preparation of powders,which can directly alloy the raw materials into target powders in a relatively low cost way.
机械合金化是一种制备粉末材料的常用方法,能够将原始粉末通过球磨直接合成合金粉末,制备出熔炼法无法合成的材料,具有低成本的优势。
6) mechanical alloying
机械合金化
1.
Effect of mechanical alloying on the property of Mo-Cu alloy;
机械合金化对Mo-Cu合金性能的影响
2.
Synthesis of CoSb_3 thermoelectric material by mechanical alloying and spark plasma sintering;
机械合金化与等离子体烧结法制备CoSb_3热电材料
3.
Study of nickel's effect on the synthesis of TiC during mechanical alloying;
Ni在机械合金化合成TiC过程中的研究
补充资料：机械合金化法制粉
机械合金化法制粉
mechanical alloying process to produce powder
机械合金化法制粉mechanieal alloyi吧proeessto Preduce powder以两种以上成分的金属和非金属微细粉为原料，在机械运动的作用下制取化学成分复杂、显微结构细小的复合合金粉的方法(见机械合金化)。通常，合金粉多采用雾化法制取，但很难获得掺有非金属质点的微细合金粉。机械合金化法则能够制造每个颗粒几乎含有全部原始配料成分，其结构呈嵌有硬质点金属化合物颗粒的复合粉。 机械合金化法最早专门用于制取镍基或铁基弥散强化型高温合金粉。所用原料可选1一200召m的各种纯金属粉，包括镍、铬、铁、钻、钨、铂、妮等。对于活性金属则应以其低合金形式加入。例如，含有大量铝、钦、错、铅的镍基母合金质脆，铸造状态很易破碎为粉。起弥散强化作用的非金属粉为1月m的氧化忆。由此而制取的机械合金化粉，如Ni一20 Cr一1 .0 Fe一0 .3Al一0.STi一0.6Y203粉，以热挤压或热等静压工艺成材，其熔点高，蠕变强度大，可用于制造发动机零件。由5一40尽m的纯铁粉、小于0.5别m的钦粉和小于1召m的非晶态硼粉为原料，经机械合金化处理后可制得每个顺粒嵌有微小硼粒子的具有精细的铁层和钱层结构的钦铁硼复合粉。为使翻粒完全溶解在铁钦基体中形成Nd:Fe，4B硬磁相，须将这种粉经600℃、1小时的热处理，然后用来制造高性能烧结永磁体。此外，以平均粒度为5一100刀m的铁粉和0.5尽m的碳化锭或碳化钦、氮化钦、氧化铝等为原料可制得性能良好的机械合金化粉，用于制取硬质颗粒增强型金属基复合材料。这种钢基复合材料在退火状态可被切削加工.经热处理后能改变性能，可用作刀具和模具，有新型硬质合金之称。 (王洪海)1二J.J、矛、，.‘，已，、侣目洲、J、