1) 6-calcium 2-aluminium sulfide 18-oxide 6-hydrate
三元型含水硫铝酸钙
1.
Study of thermodynamics of 4-calcium 2-aluminium sulfide 10-oxide 12-hydrate and 6-calcium 2-aluminium sulfide 18-oxide 6-hydrate;
一元和三元型含水硫铝酸钙热力学研究
2) 4-calcium 2-aluminium sulfide 10-oxide 12-hydrate
一元型含水硫铝酸钙
3) 3CaO·Al 2O 3·CaSO 4·12H 2O
含水硫铝酸钙
5) Ba_bearing calcium sulphoaluminate
含钡硫铝酸钙
1.
Based on C 4A 3S(3CaO·3Al 2O 3·CaSO 4) which is the main mineral in sulphoaluminate cement, the Ba_bearing calcium sulphoaluminate series of new cement mineral are synthesized by substitution of analytical pure chemical reagent BaCO 3, BaSO 4 for Ca ions.
以硫铝酸盐水泥的主要矿物Ｃ４Ａ３Ｓ（３ＣａＯ·３Ａｌ２Ｏ３·ＣａＳＯ４）为基础，用分析纯化学试剂ＢａＣＯ３ ，ＢａＳＯ４ 对Ｃ４Ａ３Ｓ中的Ｃａ 离子进行取代，合成了一种新水泥矿物———含钡硫铝酸钙系列矿物，并研究了该系列矿物的强度发展规律。
6) calcium sulphoaluminate
无水硫铝酸钙
1.
Under the process conditions,qualified sulphoaluminate cement clinker can be produced and main mineral composition of cement clinker are calcium sulphoaluminate and dicalcium silicate.
结果表明:用本试验所采用的原料,配料比为m(矾土)∶m(石灰石)∶m(脱硫石膏)=35∶43∶22,煅烧温度为1400℃可烧制成矿物组成为无水硫铝酸钙和硅酸二钙的合格硫铝酸盐水泥熟料。
补充资料：水化硫铝酸钙
分子式：
CAS号：
性质：铝酸三钙或硫铝酸钙在石膏存在时的水化产物，有高硫型和低硫型两类。若硫酸钙含量充足，则生成三硫酸盐型硫铝酸钙，其化学式为3CaO·Al2O3·3CaSO4·30～32H2O，又称钙钒石，其中铝可被铁置换，简写为AFt。若硫酸钙含量较少，则生成单硫酸盐型硫铝酸钙AFm，化学式3CaO·Al2O3·CaSO4·nH2O，其中最常见的是3CaO·Al2O3·CaSO4·12H2O，晶体为假六方板状或针尖状。密度1.99g/cm3。一轴晶负光性。一轴晶非常光折射率no=1.504，常光折射率ne=1.488。水化硫铝酸钙在快硬快凝水泥水化时是水泥石产生早期强度的主要成分。
CAS号：
性质：铝酸三钙或硫铝酸钙在石膏存在时的水化产物，有高硫型和低硫型两类。若硫酸钙含量充足，则生成三硫酸盐型硫铝酸钙，其化学式为3CaO·Al2O3·3CaSO4·30～32H2O，又称钙钒石，其中铝可被铁置换，简写为AFt。若硫酸钙含量较少，则生成单硫酸盐型硫铝酸钙AFm，化学式3CaO·Al2O3·CaSO4·nH2O，其中最常见的是3CaO·Al2O3·CaSO4·12H2O，晶体为假六方板状或针尖状。密度1.99g/cm3。一轴晶负光性。一轴晶非常光折射率no=1.504，常光折射率ne=1.488。水化硫铝酸钙在快硬快凝水泥水化时是水泥石产生早期强度的主要成分。