1) center layer segregation
中心层偏析
1.
The center layer segregation and its mechanism of 1235 alloy cast-rolling stock were discussed.
主要阐述了1235合金铸轧带材生产时中心层偏析产生的机制,对比分析不同铸轧参数条件下的中心层偏析情况,提出减轻或消除中心层偏析的措施。
2) centerline segregation
中心偏析
1.
Original position statistic distribution analysis of the centerline segregation and the inclusion distribution in the cross section of continuous casting slab under different drawing speed technology conditions;
不同拉速工艺下连铸板坯横截面中心偏析和夹杂物的原位统计分布分析
2.
The causes and the countermeasures of centerline segregation of slabs in No. 2 Steelmaking plant of HISCO;
邯钢二炼钢厂板坯中心偏析的成因及对策
3.
Application of dynamic soft reduction technology in the control of centerline segregation of medium carbon steel slab
动态轻压下在中碳钢铸坯中心偏析控制中的应用
3) central segregation
中心偏析
1.
Effect of electromagnetic stirring at secondary cooling area on central segregation of a continuously cast slab;
二冷区电磁搅拌对连铸板坯中心偏析的影响
2.
When the reduction amount exceeds this value,there is no visible improvement of central segregation while the.
压下量一般以6~7 mm为宜,超过此值后压下量继续增加,中心偏析无明显改善,中心裂纹却增加。
3.
According to the analysis results from the database of the sulfur print of slab in An steel,the technological parameters influencing central segregation in micro-alloyed steels were analyzed.
根据鞍钢管线钢连铸坯硫印分析结果数据库,对影响中心偏析的工艺进行了系统的分析。
4) center segregation
中心偏析
1.
Influencing factors on center segregation in continuously cast Nb-V-Ti-contained micro-alloying slabs;
含铌钒钛微合金化钢连铸板坯中心偏析的影响因素
2.
Practice in controlling center segregation of continuons casting slab
控制连铸板坯中心偏析的实践
3.
The distribution of elements,center segregation,porosity,inclusions and so on in the cross section of automobile beam slab were investigated by original position statistic distribution analysis(OPA) technique.
采用金属原位分析技术对汽车大梁钢坯横截面上各元素的成分分布、中心偏析、疏松、夹杂等进行质量分析。
5) centreline segregation
中心偏析
1.
The formation of centreline segregation in continuously cast billet has been simulated based on the continuum model and the effect of the interdendritic liquid flow on the centreline segregation is analyzed.
基于连续模型对连铸方坯的中心偏析进行了数值模拟,分析了枝晶间液相流动对铸坯中心偏析的影响。
2.
These system can simulate the centreline segregation ratio and accurately control the soft reduction acting at the solidification end of the slab,thus the centreline segregation ratio and center loosen will be reduced,and the quality of continuous casting slab will be greatly improved.
RAM动态轻压下系统,采用了衡阳镭目公司最新开发的连铸坯凝固模型、动态轻压下控制模型和伺服执行系统等,对连铸坯的中心偏析进行数值模拟,精确地对连铸坯凝固末端实施动态轻压下,从而降低了铸坯中心偏析、中心疏松的程度,大大提高了铸坯产品质量。
6) center carbon segregation
中心碳偏析
1.
The evolvement analysis on center carbon segregation of U74 heavy rail steel bloom after blooms rolling;
U74重轨大方坯开坯后中心碳偏析的演变分析
2.
Effect of Concasting Technology Parameters on Center Carbon Segregation of High Carbon Steel Billet;
连铸工艺参数对高碳钢小方坯中心碳偏析的影响