1) alloying annealing
合金化退火
1.
The results showed that at 450 ℃ the coating was η phase at the time stage of the beginning of alloying annealing,part ζ phase transformed to the coating surface .
研究表明,450℃时在合金化退火开始时间段镀层为η相,20 s左右部分ζ相长至镀层表面,30 s后表面主要为ζ相,随着退火时间的延长到300 s镀层大部分为δ相,不再发生相变,合金化结束;500℃时合金化过程基本与450℃一致,但退火3 s后表面就已出现少量的ζ相,而9 s后表面基本由δ相和ζ相混合组成,退火时间达到20 s后表面已完全为δ相;550℃时退化3 s后表面出现少量的δ相,到9 s后镀层几乎全部由δ相组成。
2) Mechanical alloying with annealing treatment
机械合金化-真空退火
3) annealed Al-alloy
退火铝合金
4) alloy ingot annealing
合金锭退火
5) annealed metals
退火金属
6) spheroidal annealing
球化退火
1.
Production of spheroidal annealing of cold rolled 25 steel strip;
25钢冷轧球化退火钢带的生产
2.
To introduce a new process for making needle latch steel wire with diameter range 0 34～0 53mm The technological process consists of patenting-phosphating-cold drawing-spheroidal annealing under Ac 1 point in electrical heating furnace-slight drawing to finished product The theoretical basis and advantages of the main points of new process are emphatically elaborate
该工艺流程是：铅淬火—磷化—拔丝—Ａｃｌ以下电加热连续退火炉球化退火—轻拉至成品。
补充资料：软化退火(见低温退火)
软化退火(见低温退火)
soft-annealing
rU0nhUO tUihUO软化退火(soft一annealing)见低温退火。