1) eutectic film
共熔薄层
2) co-crystal temperature
共熔
1.
The experimental results of the co-crystal and co-melting temperatures of the typical food materials in this study shows the tend that co-crystal temperature is lower than co-melting temperature, and the tangent value of the curve of co-crystal temperature is bigger than that of the co-melting temperature.
实验研究和分析结果表明一些典型食品物料的共晶温度比共熔温度低;共晶曲线比共熔曲线的斜率变化大;物料晶核形成阶段的电阻变化率小于物料大冰晶成长阶段的电阻变化率,进而又小于物料共晶阶段的电阻变化率。
3) eutectic mixture
低共熔物
1.
DNTF can form eutectic mixture with TNT and in liquid phase carriers having different m.
另外 ,DNTF能与梯恩梯 (TNT)形成低共熔物 ,可以调配成不同熔点、不同能量要求的液相载体 ,为熔铸炸药的发展开辟了新领
2.
According to the theoretical calculation, the weight compositions, phase change temperatures and enthalpy of fatty acids eutectic mixtures were evaluated by DSC.
利用凝固点下降理论,结合DSC热分析技术研究确定了脂肪酸二元体系低共熔物的组成、相变温度和相变焓。
4) eutectic point
低共熔点
1.
The experimental results showed:NaSCN-NaAc--NaI ternary system is of the eutectic type,and the eutectic point is located at 504 K and consists of 19.
用目测变温法研究了ＮａＳＣＮ－ＮａＡｃ－ＮａＩ三元系的相图，结果表明：ＮａＳＣＮ－ＮａＡｃ－ＮａＩ三元体系为低共熔型相图，它的低共熔点的温度为５０４Ｋ，组成为（ｍ％）：ＮａＩ（１９。
5) Eutectic
低共熔体
6) eutectic bonding
共熔键合
1.
A novel Si/Ti/Au/Au/Ti/Si bonding method based on Au/Si eutectic bonding in nitrogen atmosphere was presented.
运用Si/Ti/Au/Au/Ti/Si在N2保护下及420℃左右,成功地实现了Au/Si共熔键合,成品率达到90%以上。
参考词条
补充资料：低共熔聚合物
分子式：
CAS号：
性质： 能与其他结晶物质相互混溶并在低温下具有低共熔点的聚合物。利用低共熔结晶的方法，可以获得具有特殊结晶形态的聚合物。例如，聚乙烯与1,2,4,5-四氯代苯组成低共熔体系，在高温下形成溶液，在低温下结晶，并具有低共熔点。如将得到的低共熔混合物淬火至室温，四氯代苯升华逸出，最终可获得具有微丝晶结构的聚乙烯。
CAS号：
性质： 能与其他结晶物质相互混溶并在低温下具有低共熔点的聚合物。利用低共熔结晶的方法，可以获得具有特殊结晶形态的聚合物。例如，聚乙烯与1,2,4,5-四氯代苯组成低共熔体系，在高温下形成溶液，在低温下结晶，并具有低共熔点。如将得到的低共熔混合物淬火至室温，四氯代苯升华逸出，最终可获得具有微丝晶结构的聚乙烯。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。