1) slurry erosion
砂浆冲蚀
1.
Two different HVOF spray systems were used to prepare six WC–10Co–4Cr coatings on 0Cr13Ni5Mo stainless steel using three commercial powders, and the slurry erosion behavior of coatings and the substrate was investigated on a self-manufactured slurry pot erosion tester.
以2种不同的HVOF喷涂系统和3种商用粉末在0Cr13Ni5Mo基材上喷涂6种WC–10Co–4Cr涂层,用自行研制的料浆罐冲蚀设备对涂层和基材的砂浆冲蚀行为进行了研究,分析了显微结构和显微硬度对涂层冲蚀性能的影响及涂层冲蚀后的表面形貌。
2) slurry wear
砂浆冲蚀磨损
1.
The slurry jet test apparatus was used for the slurry wear test.
采用砂浆喷射装置,砂浆流速为10~40 m/s,冲击角为90°~15°,对比研究了该复相陶瓷和3Y-TZP陶瓷的砂浆冲蚀磨损。
3) Mortar Corrosion
砂浆腐蚀
4) erosion sand plug
冲蚀砂柱
5) sand blast erosion
喷砂冲蚀
6) slurry erosion
浆体冲蚀
1.
Study of slurry erosion resistance of Cu-base and Ni-base flame spray welding coating;
Cu基、Ni基喷焊层材料的浆体冲蚀性能研究
2.
The slurry erosion and cavitation erosion resistance of the coatings have been investigated.
用氧乙炔焰喷焊法制备了NiCrSiB及其加入WC陶瓷颗粒的复合覆层材料,用光学显微镜分析了覆层的显微组织,并对覆层材料的浆体冲蚀和气蚀抗力进行了研究,用扫描电子显微镜对覆层表面气蚀破坏形貌进行了观察。
3.
The slurry erosion resistance of the test coatings has been investigated.
采用氧乙炔焰喷焊法制备 Ni基覆层材料及其加入 WC陶瓷颗粒的复合覆层材料 ,用光学显微镜分析覆层材料的金相组织 ,对覆层材料的浆体冲蚀抗力进行对比研究。
补充资料：冲蚀
冲蚀
erosion corrosion
ehongsh-冲蚀(erosion corrosion)金属材料表面与腐蚀流体冲刷的联合作用，而引起材料局部的金属腐性。在发生这种腐蚀时，金属离子或腐蚀产物因受高速腐蚀流体冲刷而离开金属材料表面，使新鲜的金属表面与腐蚀流体直接接触，从而加速了腐蚀过程。若流体中悬浮较硬的固体颗粒，则将加速材料的损坏。一般说来，流体的速度愈高，流体中悬浮的固体颗粒愈多、愈硬，冲刷腐蚀速度愈快。腐蚀介质流动速度又取决于流动方式:层流时，由于流体的粘度，在沿管道截面有一种稳态的速度分布;湍流时，破坏了这种稳态速度分布，这不仅加速了腐蚀剂的供应和腐蚀产物的迁移，而且在流体与金属之间产生切应力，能剥离腐蚀产物，从而加大了冲蚀速度。因此，在管道的拐弯处及流体进入管道或贮罐处容易产生这种破坏。另外，金属表面成膜的特征也可以影响冲蚀速度。硬的、致密的、连续的、粘附性强的膜冲蚀速度小，反之则大。抑制或减少冲蚀的措施是:选择耐蚀性和耐磨性好的材料;改变腐蚀环境如添加缓蚀剂，过滤悬浮固体粒子，降低温度，减小流速和湍流;采用栖牲阳极作阴机保护等。 (1陈树俊l)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条