1) niobium-based ultrahigh-temperature alloy
Nb基超高温合金
1.
At present, niobium-based ultrahigh-temperature alloys are usually prepared by multiple arc-melting in order to get uniform as-cast ingots.
目前Nb基超高温合金的制备主要是通过多次电弧熔炼得到成分均匀的铸锭。
2) Nb-Ti-Si based ultrahigh temperature alloy
Nb-Ti-Si基超高温合金
1.
The master alloy ingot of Nb-Ti-Si based ultrahigh temperature alloy was prepared by vacuum nonconsumable arc melting.
采用真空非自耗电弧熔炼法制备Nb-Ti-Si基超高温合金的母合金锭,分别于1300、1400、1500和1600℃保温50h,对其进行均匀化处理,然后于1100℃保温50h进行时效处理。
3) Ti-Nb-Si based ultrahigh temperature alloy
Ti-Nb-Si基超高温合金
1.
Microstructures of Si-Cr co-depositing coatings prepared on Ti-Nb-Si based ultrahigh temperature alloy
Ti-Nb-Si基超高温合金Si-Cr共渗抗氧化涂层的显微组织
4) Nb-based high temperature alloy
Nb基高温合金
1.
Alloying is a useful method to enhance the mechanical properties of Nb-based high temperature alloy.
综述了近年来国内外在合金化改善Nb基高温合金组织形貌、提高力学性能方面所取得的进展,分析了Ti,Cr,Hf和Mo等合金化元素对合金中Laves相,亚稳相Nb_3Si和γ-Nb_5Si_3的影响,总结了合金元素对材料力学性能的影响规律。
5) advanced niobium-silicide based ultrahigh temperature alloy
新型Nb硅化物基超高温合金
1.
An advanced niobium-silicide based ultrahigh temperature alloy was prepared by vacuum consumable arc-melting method.
本文设计了新型Nb硅化物基超高温合金的成分，并采用真空自耗电弧熔炼法制备了其母合金锭。
6) Nb-Mo-Si super alloys
Nb-Mo-Si超高温合金
补充资料：超因瓦合金
分子式：
CAS号：
性质：用钴置换因瓦合金中的部分镍制得的一种铁镍钴合金。其标准成分为：30％～32％镍，4.5％～6.5％钴，≤0.5％碳，≤0.4％锰，≤0.2％硅，余为铁。牌号为Ni31Co5。退火组织为单相奥氏体。经过870℃固溶处理和300℃时效后，其膨胀系数低于因瓦合金，如20℃小于0.2×106/℃，故名。
CAS号：
性质：用钴置换因瓦合金中的部分镍制得的一种铁镍钴合金。其标准成分为：30％～32％镍，4.5％～6.5％钴，≤0.5％碳，≤0.4％锰，≤0.2％硅，余为铁。牌号为Ni31Co5。退火组织为单相奥氏体。经过870℃固溶处理和300℃时效后，其膨胀系数低于因瓦合金，如20℃小于0.2×106/℃，故名。